VERSIFY™ 2200
| Category: | POP , Plastomer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | VERSIFY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hZwuZC_VERSIFY-2200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VERSIFY™ 2200 Plastomer is a resin with a low melt flow rate making it suitable for blown film, blow molding, extrusion and thermoforming. It is an excellent sealant and is particularly suitable for use in BOPE structures. It has excellent compatibility with PP and is an useful agent to bring softness and temperature performance. Main Characteristics
Applications
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.876 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Total Crystallinity | 21 | % | Internal Method |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ultimate Seal Strength Temperature (50.8 µm) | 80 | °C | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness 1 | ASTM D2240 | ||
| Shore A, Compression Molded | 94 | ||
| Shore D, Compression Molded | 42 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, Compression Molded) | 20.5 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, Compression Molded) | 690 | % | ASTM D638 |
| Flexural Modulus - 1% Secant (Compression Molded) | 99.9 | MPa | ASTM D790 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| Secant Modulus | ASTM D882 | ||
| 2% Secant, MD : 51 µm | 86.5 | MPa | |
| 2% Secant, TD : 51 µm | 94.4 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 51 µm | 10.7 | MPa | |
| TD : Yield, 51 µm | 10.1 | MPa | |
| MD : Break, 51 µm | 29.5 | MPa | |
| TD : Break, 51 µm | 26.3 | MPa | |
| Elmendorf Tear Strength 3 | ASTM D1922 | ||
| MD : 51 µm | 590 | g | |
| TD : 51 µm | 1300 | g | |
| Seal Initiation Temperature 4(51 µm) | 60.0 | °C | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -24.0 | °C | Internal Method |
| Vicat Softening Temperature | 63.0 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 82.2 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Gloss | ASTM D523 | ||
| 20°, 1000 µm, Compression Molded | 110 | ||
| 60°, 1000 µm, Compression Molded | 128 | ||
| Haze (39400 µm, Injection Molded) | 4.8 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Hardness after 10 seconds. |
| 2 . | 50 mm/min |
| 3 . | Method B |
| 4 . | Temperatures at which 1 lb/in. (4.4 N/25.4 mm) heat seal strength is achieved. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nypol® PA A3 G30 HL CNZA178 NR466 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| CompaDur® 125 GF 15 natural (014) | DimeLika Plast GmbH | PBT+PET | CompaDur® |
| DIOSHY® TPEE E930D-GS | DIOSHY Co.,Ltd. | TPEE | DIOSHY® |
| Hifax TYC 900P | LyondellBasell Industries | PP Impact Copolymer | Hifax |
| Lushan EF-3 | Guangzhou Lushan New Materials Co., Ltd | Polyolefin, Unspecified | Lushan |