Ebalta GM 984-1 / Comp. A+B
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | Ebalta Kunststoff GmbH |
| Trademark: | Ebalta |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hZVKiO_Ebalta-GM-984-1-Comp-A-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This product is a polyurethane system. GM 984-1 Comp. B (Amine) can be subject to colour variations due to raw materials, but these colour variations have no influence on the quality and the properties of the product. The postcured material is not UV stable and darkens by and by. However according to our experience the change in colour does not affect its utilizability. Physical final properties will be achieved after 7 days' curing at room temperature or after postcuring for 8 hrs. at 80°C. As bonding agent on aluminium support we recommend our PU coupling paste KP 8. Applications
Properties
|
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness (Shore D) | 63 - 67 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 37.0 - 41.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 300 - 320 | % | ISO 527-2 |
| Flexural Modulus | 747 - 827 | MPa | ISO 178 |
| Flexural Stress | 27.0 - 29.0 | MPa | ISO 178 |
| Taber Abrasion Resistance (500 Cycles, 500g, H-18 wheel) | 17.0 | mg | Internal method |
| Flexural Strain at Flexural Strength | 6.5 - 7.5 | % | ISO 178 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Resin | Mixing ratio by weight: 100 | ||
| Hardening method | Mixing ratio by weight: 130 |
| Additional Information |
|---|
| Wear jet test : 41 W(V/t) [mm³/min] (internal tests) |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Density (20°C) | 1.13 - 1.17 | g/cm³ | |
| Viscosity (25°C) | 2.5 - 2.9 | Pa·s | |
| Curing Time (20°C) | 12 - 16 | hr | |
| Pot Life 1(20°C) | 30 - 45 | min |
| Note Message | |
|---|---|
| 1 . | 200 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3880 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| GPPC PS-302 | GPPC Chemical Co., Ltd. | PS (HIPS) | GPPC |
| Kepamid® 2300SF | Korea Engineering Plastics Co., Ltd | Nylon 66 | Kepamid® |
| ESTOPLAST XU 6233BB02 | Ester Industries Ltd. | Nylon 66 | ESTOPLAST XU |
| Sylvin 6034-85 Grey 9621 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |