Order Products : sales@su-jiao.com
EPO-TEK® OE120
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Epoxy Technology Inc. |
| Trademark: | EPO-TEK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hWAqng_EPO-TEK-OE120.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A two component, opaque epoxy, designed for fiber optics packaging applications. It is a black-colored version of EPO-TEK 353ND-T. It has a high Tg for resisting elevated operating temperatures found in medical fiber optics or hybrid-microelectronic applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Particle Size | < 50.0 | µm |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Degradation Temperature | 402 | °C | |
| Die Shear Strength - >15 kg (23°C) | 35.2 | MPa | |
| Operating Temperature | |||
| Continuous | -55 to 250 | °C | |
| Intermittent | -55 to 350 | °C | |
| Storage Modulus (23°C) | 3.18 | GPa | |
| Thixotropic Index | 3.30 | ||
| Weight Loss on Heating | |||
| 200°C | 0.070 | % | |
| 250°C | 0.38 | % | |
| 300°C | 1.1 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature 1 | > 90.0 | °C | |
| CLTE - Flow | |||
| -- 2 | 2.8E-5 | cm/cm/°C | |
| -- 3 | 1.2E-4 | cm/cm/°C |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 10 | ||
| Part B | Mix Ratio by Weight: 1.0 | ||
| Shelf Life (23°C) | 26 | wk |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Color | |||
| -- 4 | Amber | ||
| -- 5 | Black | ||
| Density | |||
| Part B | 1.06 | g/cm³ | |
| Part A | 1.21 | g/cm³ | |
| Viscosity 6(23°C) | 12 to 16 | Pa·s | |
| Curing Time (150°C) | 1.0 | hr | |
| Pot Life | 210 | min |
| Cured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Shore Hardness (Shore D) | 85 | ||
| Lap Shear Strength (23°C) | > 13.8 | MPa | |
| Relative Permittivity (1 kHz) | 3.47 | ||
| Volume Resistivity (23°C) | > 6.0E+12 | ohms·cm | |
| Dissipation Factor (1 kHz) | 0.010 |
| Note Message | |
|---|---|
| 1 . | Dynamic Cure 20-200°C/ISO 25 Min; Ramp -10-200°C @ 20°C/Min |
| 2 . | Below Tg |
| 3 . | Above Tg |
| 4 . | Part B |
| 5 . | Part A |
| 6 . | 20 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 384 HEC TFE 15 | RTP Company | PC | RTP |
| Shanghai Potomer SG5 | Shanghai Potomer International Trade Co., Ltd. | PVC, Rigid | Shanghai Potomer |
| Westlake HDPE MC2004 | Westlake Chemical Corporation | HDPE | Westlake HDPE |
| Edgetek™ PC-10GF/000 FR WT088 | PolyOne Corporation | PC | Edgetek™ |
| LNP™ THERMOCOMP™ PX87791 compound | SABIC Innovative Plastics | Nylon 6 | LNP™ THERMOCOMP™ |