EVAL™ F101
| Category: | EVOH , Ethylene Vinyl Alcohol |
| Manufacturer: | Kuraray Co., Ltd. |
| Trademark: | EVAL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hW97Kp_EVAL-F101.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
32 mol% Ethylene Vinyl Alcohol Copolymer F101A - non-lubricated pellets F101B - Pellets are lubricated to facilitate material feeding into extruder |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 1.6 | g/10 min | |
| 210°C/2.16 kg | 3.8 | g/10 min | |
| Ethylene Content | 32.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 100 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2700 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 34.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 15 | % | ISO 527-2 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Permeability | ISO 14663-2 | ||
| 20°C, 0% RH | 3.9E-3 | cm³·mm/m²/atm/24 hr | |
| 20°C, 65% RH | 7.9E-3 | cm³·mm/m²/atm/24 hr | |
| 20°C, 85% RH | 0.030 | cm³·mm/m²/atm/24 hr | |
| Water Vapor Transmission Rate 1(40°C, 90% RH) | 1.6 | g·mm/m²/atm/24 hr | ASTM E96 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 69.0 | °C | ISO 11357-2 |
| Melting Temperature | 183 | °C | ISO 11357 |
| Peak Crystallization Temperature | 161 | °C | ISO 11357-3 |
| Note Message | |
|---|---|
| 1 . | Procedure E |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® BZMO 30 | Arkema | Nylon 11 | Rilsan® |
| TOTAL Polypropylene PPH 3962 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| Yuyao PBT 3060G30 | Yuyao Tenglong Plastics Co., Ltd. | PBT | Yuyao PBT |
| Andur 80-5AP/Curene® 280 | Anderson Development Company | PUR-Ether/TDI | Andur |
| LNP™ THERMOCOMP™ DX14354X compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ THERMOCOMP™ |