AKROMID® B3 GF 40 black (3383)
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hVDbEm_AKROMID-B3-GF-40-black-3383-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® B3 GF 40 black (3383) is a 40% glass fibre reinforced polyamide 6 with high rigidity and strength Applications are mainly components in mechanical engineering and in the automotive industry |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.45 | -- | g/cm³ | ISO 1183 |
| Spiral Flow | 48.0 | -- | cm | Internal Method |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.80 | -- | % | |
| Flow | 0.30 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 12800 | 8200 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 210 | 130 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 4.0 | 5.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 10300 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 300 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | 14 | -- | kJ/m² | |
| -30°C | 14 | -- | kJ/m² | |
| 23°C | 18 | 23 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -40°C | 110 | -- | kJ/m² | |
| -30°C | 110 | -- | kJ/m² | |
| 23°C | 110 | 110 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -40°C | 14 | -- | kJ/m² | |
| 23°C | 20 | -- | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 215 | -- | °C | ISO 75-2/A |
| Melting Temperature 3 | 222 | -- | °C | DIN EN 11357-1 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 4(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Reinforcement Content | 40 | -- | % | ISO 1172 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10 K/min, DSC |
| 4 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Staramide P1000J5 | Eurostar Engineering Plastics | Nylon 6 | Staramide |
| NuSil MED-4820 | NuSil Technology | Silicone Rubber, LSR | NuSil |
| Karina CLEAR PVC COMPOUND 70850/200-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lupolen 4261 AG UV | LyondellBasell Industries | HDPE | Lupolen |
| CYCOLOY™ CX7240U resin | SABIC Innovative Plastics | PC+ABS | CYCOLOY™ |