Hifax CA1147A
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hifax |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hUu8iq_Hifax-CA1147A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hifax CA 1147 A is a thermoplastic polyolefin developed for extrusion processes, particularly for the Wire & Cable industry. Thanks to its high rubber content and structure, the main features are low stiffness, low hardness, combined with a high melting point and a medium fluidity. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.890 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.5 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 28 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break, 23°C) | 11.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 800 | % | ISO 527-2 |
| Flexural Modulus | 80.0 | MPa | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 57.0 | °C | ISO 306/A50 |
| Additional Information |
|---|
| Tensile Stress at Break, ISO 527, 23°C: >11 MPaTensile Strain at Break, ISO 527: >800% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® AR35BK8502 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| NuSil CV-2943 | NuSil Technology | Silicone | NuSil |
| Kelon® A FR H2 CETG/300-V0 | LATI S.p.A. | Nylon 66 | Kelon® A |
| Karina CRYSTAL PVC COMP (SP31493) -E 70/265-NT | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina WHITE PVC COMPOUND 550-10/10-IS-SD-AS (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |