Zytel® HTN FR52G20NH NC010
| Category: | PPA , HIGH PERFORMANCE POLYAMIDE RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® HTN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hUmkaP_Zytel-HTN-FR52G20NH-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 20% Glass Reinforced, Flame Retardant, Non-Halogenated, PPA, High Performance Polyamide |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Part Marking Code (SAE J1344) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.36 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.1 | -- | % | |
| Flow | 0.30 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 8200 | 8600 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 135 | 120 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.4 | 2.2 | % | ISO 527-2 |
| Flexural Modulus | 7800 | 8200 | MPa | ISO 178 |
| Flexural Stress | 215 | 180 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 6.0 | -- | kJ/m² | |
| 23°C | 6.0 | 6.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 40 | 30 | kJ/m² | |
| 23°C | 40 | 36 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 276 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 310 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 2.5E-5 | -- | cm/cm/°C | |
| Flow : -40 to 23°C | 2.7E-5 | -- | cm/cm/°C | |
| Flow : 55 to 160°C | 2.1E-5 | -- | cm/cm/°C | |
| Transverse | 6.8E-5 | -- | cm/cm/°C | |
| Transverse : -40 to 23°C | 6.4E-5 | -- | cm/cm/°C | |
| Transverse : 55 to 160°C | 1.0E-4 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Electric Strength | 42 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.750 mm | V-0 | -- | ||
| 1.50 mm | V-0 | -- | ||
| Glow Wire Flammability Index (0.400 mm) | 960 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (0.400 mm) | 725 | -- | °C | IEC 60695-2-13 |
| Oxygen Index | 35 | -- | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | First Heat |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC M8184 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| RTP 200 C TFE 10 | RTP Company | Nylon 11 | RTP |
| Nypol® PA A3 TZ PRTA010 NR355 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| KOPLA PET KEG1030F | KOPLA Co., Ltd. | PET | KOPLA PET |
| INLUBE PA612CF30TF13SI2 | Infinity LTL Engineered Compounds | Nylon 6/12 | INLUBE |