Kepamid® 2325GVS
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Korea Engineering Plastics Co., Ltd |
| Trademark: | Kepamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hSqOVY_Kepamid-2325GVS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KEPAMID 2325GVS is a 25% glass fiber reinforced and flame retardant polyamide-66. UL94 V-0 flame resistance with good mechanical and thermal properties. It is applicable to automotive, electrical, electronic, and industrial parts. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.54 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (275°C/2.16 kg) | 11 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.30 to 0.80 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 137 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 3.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 8340 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 206 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 69 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 255 | °C | |
| 1.8 MPa, Unannealed | 235 | °C | |
| Melting Temperature | 260 | °C | DSC |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Hopper Temperature | 260 to 300 | °C | |
| Rear Temperature | 260 to 300 | °C | |
| Middle Temperature | 260 to 300 | °C | |
| Front Temperature | 260 to 300 | °C | |
| Nozzle Temperature | 260 to 300 | °C | |
| Mold Temperature | 40.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ DC-818.G001-8000 | PolyOne Corporation | PP, Unspecified | Maxxam™ |
| TECHNYL® A 31T1 MZ40 GREY 174 N | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| AKROMID® B3 1 black (2501) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| LEXAN™ I2120 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| Karina GREEN COLOR CONCENTRATE 40/447-FC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |