SABIC® LDPE HP4027N
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | SABIC Americas, Inc. |
| Trademark: | SABIC® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hSSoTB_SABIC-LDPE-HP4027N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRODUCT DESCRIPTION: SABIC® LDPE HP4027N is a Low Density Polyethylene grade without slip and anti-block additives, with increased density. It typically exhibits good draw down ability with higher output. Films typically exhibit excellent optics, good heat seal properties combined with high rigidity. TYPICAL APPLICATIONS: Surface protection films, thin general purpose films where high optics, enhanced stiffness and down gauging are required. This product is not intended for use in medical and pharmaceutical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.927 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (0.0500 mm) | 300 | MPa | ISO 527-2 |
| Tensile Stress (yield, 0.0500mm) | 13.0 | MPa | ISO 527-2 |
| Coefficient of Friction | > 80 | % | ISO 8295 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Blow-up Ratio | 2.00 - 3.00 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Film Thickness - Recommended / Available | 15 - 40 micron | ||
| Tensile Stress | ISO 527-3 | ||
| MD : Broken, 50 µm, blown film | 20.0 | MPa | ISO 527-3 |
| TD : Broken, 50 µm, blown film | 17.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 50 µm, blown film | 350 | % | ISO 527-3 |
| TD : Broken, 50 µm, blown film | 600 | % | ISO 527-3 |
| Dart Drop Impact (50 µm, Blown Film) | 90 | g | ASTM D1709 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 97.0 | °C | ISO 306/A50 |
| Melting Temperature (DSC) | 114 | °C | ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | ASTM D2457 | ||
| 20, 50.0 µm, blown film | > 80 | ASTM D2457 | |
| 60, 50.0 µm, blown film | > 115 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | < 7.0 | % | ASTM D1003 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Measured on 50 micron thickness blown film extruded at melt temperature of 170°C with BUR of 2.5 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 150 - 190 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Toughblend® PA66-1900 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | Nylon 6 | Toughblend® |
| INEOS Wire & Cable BPD3669 | INEOS Olefins & Polymers Europe | LLDPE | INEOS Wire & Cable |
| LNP™ THERMOCOMP™ EX11413 compound | SABIC Innovative Plastics | PEI | LNP™ THERMOCOMP™ |
| KMI PP KM-899IB | KMI Group, Inc. | PP Impact Copolymer | KMI PP |
| Sumiliteresin® PR-51649 BI | SBHPP | Phenolic | Sumiliteresin® |