Durethan® BKV 30 H2.0 901510
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hRIKia_DurethanBKV30H20901510.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 30 % glass fibers, injection molding, heat-aging stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | ||||
| -- | 1.36 | -- | g/cm³ | ASTM D792 |
| 23°C | 1.36 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | -- | g/cm³ | ISO 60 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction : 280°C, 2.00mm 1 | 0.69 | -- | % | ISO 294-4 |
| Vertical flow direction : 120°C, 2 hours, 2.00mm 2 | 0.13 | -- | % | ISO 294-4 |
| Flow direction : 280°C, 2.00mm 3 | 0.30 | -- | % | ISO 294-4 |
| Flow direction : 120°C, 2 hours, 2.00mm 4 | 0.060 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 7.0 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.1 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 210 | 100 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ||||
| 23°C 5 | 9200 | 5600 | MPa | ASTM D638 |
| 23°C | 9500 | 5800 | MPa | ISO 527-2/1 |
| Tensile Strength | ||||
| Fracture, 23°C | 180 | 100 | MPa | ASTM D638 |
| Fracture, 23°C | 170 | 100 | MPa | ISO 527-2/5 |
| Tensile Elongation (Break, 23°C) | 3.0 | 6.0 | % | ASTM D638, ISO 527-2/5 |
| Tensile Creep Modulus | ISO 899-1 | |||
| 1 hr | -- | 5100 | MPa | ISO 899-1 |
| 1000 hr | -- | 4100 | MPa | ISO 899-1 |
| Flexural Modulus | ||||
| 23°C | 8300 | 5000 | MPa | ASTM D790 |
| 23°C 6 | 9300 | 5000 | MPa | ISO 178/A |
| Flexural Strength | ||||
| 23°C | 280 | 170 | MPa | ASTM D790 |
| 3.5% strain 7 | 260 | 140 | MPa | ISO 178/A |
| 23°C 8 | 270 | 160 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength 9(23°C) | 4.0 | 6.0 | % |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Behavior 10(> 1.00 mm) | passed | -- | ISO 3795 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6, GHR, 14-090, GF30 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 - 0.12 | % | Karl Fisher |
| Films | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Film Puncture Energy | ISO 6603-2 | |||
| -- 11 | 3.00 | -- | J | ISO 6603-2 |
| -- 12 | 3.00 | 6.00 | J | ISO 6603-2 |
| Film Puncture Force | ISO 6603-2 | |||
| -- 13 | 860 | -- | N | ISO 6603-2 |
| -- 14 | 1000 | 1230 | N | ISO 6603-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | < 10 | 10 | kJ/m² | ISO 179/1eA |
| 23°C | 10 | 20 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 65 | 60 | kJ/m² | ISO 179/1eU |
| 23°C | 75 | 90 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ||||
| -40°C, 3.18 mm | 100 | 100 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 120 | 150 | J/m | ASTM D256 |
| -30°C | < 10 | < 10 | kJ/m² | ISO 180/1A |
| 23°C | 10 | 20 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 60 | 55 | kJ/m² | ISO 180/1U |
| 23°C | 65 | 80 | kJ/m² | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, not annealed, 3.99mm | 215 | -- | °C | ASTM D648 |
| 0.45 MPa, not annealed | 215 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed, 3.99mm | 200 | -- | °C | ASTM D648 |
| 1.8 MPa, not annealed | 200 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | ||||
| -- | 200 | -- | °C | ISO 306/B50 |
| -- | > 200 | -- | °C | ISO 306/B120 |
| Melting Temperature 15 | 222 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C | 2.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 1.0E-4 | -- | cm/cm/°C | ISO 11359-2 |
| RTI Elec | UL 746 | |||
| 0.830 mm | 120 | -- | °C | UL 746 |
| 1.50 mm | 120 | -- | °C | UL 746 |
| RTI Imp | UL 746 | |||
| 0.830 mm | 90.0 | -- | °C | UL 746 |
| 1.50 mm | 95.0 | -- | °C | UL 746 |
| RTI | UL 746 | |||
| 0.830 mm | 130 | -- | °C | UL 746 |
| 1.50 mm | 130 | -- | °C | UL 746 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | 1.0E+12 - 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Dielectric Strength | IEC 60243-1 | |||
| 23°C, 1.00 mm | 35 | 30 | kV/mm | IEC 60243-1 |
| 23°C, 3.00 mm | 40 | 35 | kV/mm | IEC 60243-1 |
| Dielectric Constant | IEC 60250 | |||
| 23°C, 50 Hz 16 | 4.00 | 15.0 | IEC 60250 | |
| 23°C, 1 MHz 17 | 4.00 | 5.00 | IEC 60250 | |
| 23°C, 100 Hz | 4.20 | 12.0 | IEC 60250 | |
| 23°C, 1 MHz | 3.80 | 4.40 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | |||
| 23°C, 50 Hz | 5.0E-3 | 0.50 | IEC 60250 | |
| 23°C, 100 Hz | 0.010 | 0.26 | IEC 60250 | |
| 23°C, 1 MHz | 0.017 0.015 | 0.078 0.16 | IEC 60250 | |
| Arc Resistance | -- | 76.0 | sec | ASTM D495 |
| Comparative Tracking Index | ||||
| Solution a | 425 | -- | V | IEC 60112 |
| -- | -- | 400 | V | ASTM D3638 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.830 mm | HB | -- | UL 94 | |
| 1.50 mm | HB | -- | UL 94 | |
| 1.60 mm | HB | -- | UL 94 | |
| 3.00 mm | HB | -- | UL 94 | |
| 3.20 mm | HB | -- | UL 94 | |
| Glow Wire Flammability Index (1.50 mm) | 700 | -- | °C | IEC 60695-2-12 |
| Oxygen Index 18 | 22 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 270 - 290 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2; MT 80°C; 600 Bar |
| 2 . | 60x60x2 |
| 3 . | 60x60x2; MT 80°C; 600 Bar |
| 4 . | 60x60x2 |
| 5 . | 1.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Pull Rate: 2 mm/min; 50% RH |
| 10 . | US-FMVSS302 |
| 11 . | -30°C |
| 12 . | 23°C |
| 13 . | -30°C |
| 14 . | 23°C |
| 15 . | 10°C/min |
| 16 . | Tinfoil Electrodes |
| 17 . | Tinfoil Electrodes |
| 18 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadraflex™ ALE-80A-B30 | Biomerics, LLC | TPU-Polyether | Quadraflex™ |
| SUPRAN® PP1330 | SAMBARK | PP, Unspecified | SUPRAN® |
| Unichem 8512N-02 | Colorite Polymers | PVC, Flexible | Unichem |
| LNP™ STAT-KON™ OEP32 compound | SABIC Innovative Plastics | PPS, Linear | LNP™ STAT-KON™ |
| Axiall PVC 3265 | Axiall Corporation | PVC, Rigid | Axiall PVC |