NILAMID® B3 H CF30
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Nilit Plastics |
| Trademark: | NILAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hQp6xV_NILAMID-B3-H-CF30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NILAMID® B3 H CF30 is a Polyamide 6 (Nylon 6) compound, 20% carbon fiber reinforced, heat stabilized. This compound is intended for injection molding. NILAMID® B3 H CF30 is primarily designed for the Automotive industry. It is also suitable for Industrial & Consumer applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.27 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 23°C | 0.30 | % | |
| Flow : 23°C | 0.15 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.80 | % | |
| Saturation, 23°C | 5.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 22000 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 220 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 8.5 | kJ/m² | |
| 23°C | 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| 23°C | 80 | kJ/m² | |
| 30°C | 68 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C | 9.0 | kJ/m² | |
| 23°C | 11 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 221 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 210 | °C | ISO 75-2/A |
| Continuous Use Temperature 1 | 130 | °C | IEC 60216 |
| Ball Pressure Test | IEC 60695-10-2 | ||
| 125°C | Pass | ||
| 165°C | Pass |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 2 | 1.0E+2 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+3 | ohms·cm | IEC 60093 |
| Electric Strength (2.00 mm) | 2.0 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (3.20 mm, Solution A) | < 100 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB | ||
| Oxygen Index | 25 | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | 20000 hr |
| 2 . | 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® K307 | Chevron Phillips Chemical Company LLC | MDPE | Marlex® |
| VESTOLIT® M 5960 | VESTOLIT GmbH & Co. KG | PVC, Unspecified | VESTOLIT® |
| Toyolac® 920-555 | Toray Resin Company | MABS | Toyolac® |
| ADEKA EP-4003S | Adeka Corporation | Epoxy | ADEKA |
| LOXIM 210 01 HB | LOXIM Industries Private Limited | PBT | LOXIM |