Larpeek 10 K/40
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Larpeek |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hQPx1T_Larpeek-10-K-40.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polyetheretherketone (PEEK). Carbon fibre. Very good chemical resistance. Very good thermal resistance. Low smoke toxicity index and optical density. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.45 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.25 to 0.45 | % | |
| Flow : 2.00 mm | 0.050 to 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 27000 | MPa | |
| 60°C | 26500 | MPa | |
| 90°C | 26500 | MPa | |
| 120°C | 26000 | MPa | |
| 150°C | 25500 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Break, 23°C | 255 | MPa | |
| Break, 60°C | 250 | MPa | |
| Break, 90°C | 240 | MPa | |
| Break, 120°C | 230 | MPa | |
| Break, 150°C | 200 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Break, 23°C | 1.1 | % | |
| Break, 60°C | 1.1 | % | |
| Break, 90°C | 1.1 | % | |
| Break, 120°C | 1.2 | % | |
| Break, 150°C | 1.2 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 45 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C, 3.20 mm) | 65 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | > 300 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | > 300 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 235 | °C | |
| Vicat Softening Temperature | > 300 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 2.0E-6 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 50 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+2 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 150 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 370 to 400 | °C | |
| Mold Temperature | 170 to 200 | °C | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Halene H E5201S | Haldia Petrochemicals Ltd. | HDPE | Halene H |
| KetaSpire® KT-820 SL45 | Solvay Specialty Polymers | PEEK | KetaSpire® |
| LEXAN™ 164R resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |
| Karina GRAY PVC COMPOUND 809D18/276-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| TECHNYL® A 218W V50 BLACK FA | Solvay Engineering Plastics | Nylon 66 | TECHNYL® |