Nypol® PA B3 ST NTLA010 NT387
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Nypol® PA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hP5T6E_Nypol-PA-B3-ST-NTLA010-NT387.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Poliamide 6 Super Tough in color natural, for injection molding and extrusion. Outstanding impact resistance. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.06 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (2.00 mm) | 1.2 | -- | % | ASTM D955 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 1800 | 540 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | |||
| Yield | 48.0 | 29.0 | MPa | |
| -- | 30.0 | -- | MPa | |
| Tensile Elongation | ASTM D638 | |||
| Yield | 4.0 | 30 | % | |
| Break 1 | 59 | -- | % | |
| Flexural Modulus | 1700 | 570 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (23°C) | 660 | 1200 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | 97.0 | -- | °C | |
| 1.8 MPa, Unannealed | 52.0 | -- | °C | |
| Melting Temperature | 215 | -- | °C | ASTM D2117 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.20 | % | |
| Processing (Melt) Temp | 220 to 260 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultramid® A3WG7 CR BK564 | BASF Corporation | Nylon 66 | Ultramid® |
| Badamid® LA70 K MoS21% | Bada AG | Nylon 66 | Badamid® |
| Grilamid® XE 4158 nat | EMS-GRIVORY | Nylon 12 | Grilamid® |
| HAIPLEN EP50 C10 Z1 | Taro Plast S.p.A. | PP Copolymer | HAIPLEN |
| omay® SE21 | Suzhou OMAY Optical Materials Co., Ltd | Film, PC | omay® |