Lustran® ABS LGA
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Styrolution |
| Trademark: | Lustran® ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hOvrUz_Lustran-ABS-LGA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lustran ABS LGA resin is a low-gloss grade of ABS (acrylonitrile butadiene styrene). This automotive injection molding grade offers an excellent balance of rigidity, impact strength, and abuse resistance. The resin is available in natural and black colors only. The consistent, clean, natural color of LGA makes it ideally suitable for use with color concentrates. Lustran ABS LGA resin is designed to meet stringent physical property and appearance requirements for low-loss automotive interior trim applications. Typical uses are pillar posts, consoles, scuff plates, map pockets, and interior quarter trim panels. As with any product, use of Lustran ABS LGA resin in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Specific Volume | 0.950 | cm³/g | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 220°C/10.0 kg | 21 | g/10 min | ASTM D1238 |
| 230°C/3.8 kg | 7.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 - 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2210 | MPa | ASTM D638 |
| Tensile Strength | |||
| Yield | 36.5 | MPa | ASTM D638 |
| Yield | 39.0 | MPa | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2410 | MPa | ASTM D790 |
| -- | 2430 | MPa | ISO 178 |
| Flexural Strength (Yield) | 72.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 170 | J/m | ASTM D256 |
| -40°C 1 | 7.7 | kJ/m² | ISO 180/1A |
| 23°C 2 | 16 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.18mm | 90.0 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 12.7mm | 92.2 | °C | ASTM D648 |
| 0.45 MPa, annealed, 3.18mm | 100 | °C | ASTM D648 |
| 0.45 MPa, annealed, 12.7mm | 102 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.18mm | 76.1 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 12.7mm | 87.2 | °C | ASTM D648 |
| 1.8 MPa, annealed, 3.18mm | 95.0 | °C | ASTM D648 |
| 1.8 MPa, annealed, 12.7mm | 100 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 107 | °C | ASTM D1525 3 |
| -- | 96.0 | °C | ISO 306/B50 |
| CLTE - Flow (-30 to 30°C) | 9.0E-5 | cm/cm/°C | ASTM D696 |
| RTI Elec (1.57 mm) | 60.0 | °C | UL 746 |
| RTI Imp (1.57 mm) | 60.0 | °C | UL 746 |
| RTI (1.57 mm) | 60.0 | °C | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 4 | 53 | mm/min | SAE J1685 |
| Flame Rating | UL 94 | ||
| 1.57 mm | HB | UL 94 | |
| 3.18 mm | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| A | 82.2 - 87.8 | °C | |
| B | 71.1 - 76.7 | °C | |
| Drying Time | |||
| A | 2.0 | hr | |
| B | 4.0 | hr | |
| Suggested Max Moisture | < 0.10 | % | |
| Suggested Shot Size | 50 - 75 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 235 - 249 | °C | |
| Middle Temperature | 241 - 254 | °C | |
| Front Temperature | 246 - 260 | °C | |
| Nozzle Temperature | 246 - 260 | °C | |
| Processing (Melt) Temp | 246 - 266 | °C | |
| Mold Temperature | 43.3 - 65.6 | °C | |
| Injection Pressure | 68.9 - 110 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.345 - 0.689 | MPa | |
| Clamp Tonnage | 2.8 - 5.5 | kN/cm² | |
| Cushion | < 6.35 | mm | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.5:1.0 |
| Injection instructions |
|---|
| Hold Pressure: 50 to 75% of Injection PressureScrew Speed: Moderate |
| Note Message | |
|---|---|
| 1 . | 4x10 mm bar |
| 2 . | 4x10 mm bar |
| 3 . | 标准 B (120°C/h), 压 力1 (10N) |
| 4 . | 2x100x355 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom PP6110F B5 | Spartech Polycom | PP, Unspecified | Spartech |
| UBE Polyethylene J1019 | UBE America, Inc. | PE, Unspecified | UBE Polyethylene |
| Addisil™ IND 1070 E | Momentive Performance Materials Inc. | Rubber | Addisil™ |
| Kepex® 3320GVS | Korea Engineering Plastics Co., Ltd | PBT | Kepex® |
| Dow ENDURANCE™ HFDB-0586 BK S | The Dow Chemical Company | TP, Unspecified | Dow ENDURANCE™ |