Catalyst PS/2 Yellow
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | Catalyst |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hLzPtb_Catalyst-PS-2-Yellow.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Catalyst PS/2 is a PE based yellow catalyst masterbatch, which accelerates the crosslinking reaction of the pipe product during its curing process that can take place by exposure of the pipe to water or steam at high temperature. Catalyst PS/2 Yellow contains a processing aid. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Density | 0.60 | g/cm³ | ISO 60 |
| Additional Information |
|---|
| Above values are typical averagesUse and DosageCatalyst PS/2 Yellow shall be used together with the silane-crosslinkable POLIDAN® compounds in the ratio of 5 to 95 parts respectively. The two components shall be mixed together before the extrusion or continuously during the process with the use of automatic feeders. Pre-dry is suggested.StorageThe product shall be stored under the following conditions: Closed and unbroken bags Ambient temperature not exceeding 40°C Indoor in order to avoid direct exposure to sunlight The product could undergo alterations due to extended period of storage. Solvay Specialty Polymers suggests the product use within 12 months from the production date printed on the packaging. Solvay Specialty Polymers accepts no liability of any kind in case the above mentioned conditions are not fulfilled.PackagingCatalyst PS/2 Black is supplied in 25 kg bags placed on pallets.Technical ServiceCatalyst PS/2 Yellow is part of the Solvay Specialty Polymers catalyst masterbatch range and is used together with the POLIDAN® compounds. Solvay Specialty Polymers Technical Service is available to assist customers with further information and advice including the start-up and also for any eventual necessity during the use of the product. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 150 - 200 | °C | |
| Cylinder Zone 2 Temp. | 150 - 200 | °C | |
| Cylinder Zone 3 Temp. | 150 - 200 | °C | |
| Cylinder Zone 4 Temp. | 150 - 200 | °C | |
| Cylinder Zone 5 Temp. | 150 - 200 | °C | |
| Head Temperature | 200 | °C | |
| Extruder Screw L/D Ratio | 25:1 ~ 30:1 | ||
| Extruder Screw Compression Ratio | >2.5:1 | ||
| Die Temperature | 210 | °C |
| Extrusion instructions |
|---|
| Typical extrusion temperatures in combination to POLIDAN® crosslinkable grades |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumikon® FM-MK275A | Sumitomo Bakelite Co., Ltd. | PPS | Sumikon® |
| DENKA Transparent Polymer TH-23 | Denka Company Limited | MMBS | DENKA Transparent Polymer |
| DynaPath™ 1906-SS | Polymer Dynamix | Nylon 6 | DynaPath™ |
| Elastollan® C 59 D | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |
| INEOS HDPE T50-800-01 | INEOS Olefins & Polymers USA | HDPE Copolymer | INEOS HDPE |