Quadrant EPP CESTILENE HD 500R
| Category: | HMWPE , High Molecular Weight Polyethylene |
| Manufacturer: | Quadrant Engineering Plastic Products |
| Trademark: | Quadrant EPP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hKNW6L_Quadrant-EPP-CESTILENE-HD-500R.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Quadrant EPP CESTILENE HD 500R is a High Molecular Weight Polyethylene product. It is available in Europe. Characteristics include:
|
| General Information | |
|---|---|
| Recycled Content |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.960 | g/cm³ | ISO 1183 |
| Water Absorption (Saturation, 23°C, 1.00 mm) | 0.010 | % | ISO 62 |
| Molecular Weight | 500000 | g/mol |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Service Temperature - Minimum | -60 | °C |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Relative Weight Loss | Internal Method | ||
| -- 1 | 350 | ||
| -- 2 | 1600 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D, 3 sec | 66 | ||
| Shore D, 15 sec | 64 | ||
| Ball Indentation Hardness | 45.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1300 | MPa | ISO 527-2/1B/1 |
| Tensile Stress (Yield) | 28.0 | MPa | ISO 527-2/1B/50 |
| Tensile Strain (Yield) | 10 | % | ISO 527-2/1B/50 |
| Nominal Tensile Strain at Break | > 50 | % | ISO 527-2/1B/50 |
| Compressive Stress | ISO 604/1 | ||
| 5% Strain | 22.0 | MPa | |
| 2% Strain | 14.5 | MPa | |
| 1% Strain | 9.00 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -- 3 | > 20 | kJ/m² | Internal Method |
| Partial Break | 85 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 44.0 | °C | ISO 75-2/A |
| Continuous Use Temperature | |||
| -- 4 | 80.0 | °C | |
| -- 5 | 120 | °C | |
| Vicat Softening Temperature | 80.0 | °C | ISO 306/B |
| Melting Temperature | 130 to 135 | °C | ISO 11357-3 |
| CLTE - Flow (23 to 100°C) | 1.5E-4 | cm/cm/°C | |
| Thermal Conductivity (23°C) | 0.40 | W/m/K |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Oxygen Index | < 20 | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | Wear test in sand/water slurry |
| 2 . | Wear test on plastics pin on rotating steel disk-tribo system |
| 3 . | Double 15° notch, DIS 11542-2 |
| 4 . | 20000 hrs |
| 5 . | Short periods |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAN T-26T | POLYMA Kunststoff GmbH & Co. KG | ABS | POLYLAN |
| Clyrell EC348P | LyondellBasell Industries | PP, Unspecified | Clyrell |
| Halene P M312 | Haldia Petrochemicals Ltd. | PP Impact Copolymer | Halene P |
| IDI SMC 46-16-60 | IDI Composites International | TS, Unspecified | IDI SMC |
| LNP™ STAT-KON™ DX09301C compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ STAT-KON™ |