Machine Cast MC-90 A/B
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | BJB Enterprises, Inc. |
| Trademark: | Machine Cast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hGc8zg_Machine-Cast-MC-90-A-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
The MC-90 A/B system is a production oriented fast gel and fast de-mold system. It features a mix ratio and working time ideal for machine dispensing and rapid part mold cycling, for production applications. PRODUCT HIGHLIGHTS:
|
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- 1 | 1.06 | g/cm³ | |
| -- | 1.11 | g/cm³ | |
| -- 2 | 1.12 | g/cm³ | |
| Specific Volume | 0.918 | cm³/g |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gel Time | 1.8 | min | |
| Work Time 3(25°C) | 1.3 | min |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage - Flow | 0.65 | % | ASTM D2566 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 85 to 95 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% Strain | 3.87 | MPa | |
| 200% Strain | 5.18 | MPa | |
| 300% Strain | 6.35 | MPa | |
| Tensile Strength (Yield) | 19.7 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 550 | % | ASTM D412 |
| Tear Strength | 52.5 | kN/m | ASTM D624 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100, Mix Ratio by Volume: 100 | ||
| Part B | Mix Ratio by Weight: 95, Mix Ratio by Volume: 100 | ||
| Shelf Life | 26 | wk | |
| Thermoset Mix Viscosity | ASTM D2393 | ||
| 25°C 4 | 1500 | cP | |
| 25°C 5 | 2300 | cP | |
| 25°C 6 | 1900 | cP | |
| Demold Time (25°C) | 10 | min | |
| Post Cure Time (25°C) | 120 to 170 | hr |
| Note Message | |
|---|---|
| 1 . | Part B |
| 2 . | Part A |
| 3 . | 100g mass |
| 4 . | Part B, Brookfield |
| 5 . | Part A, Brookfield |
| 6 . | Mixed, Brookfield |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Starflam PX06012 | Eurostar Engineering Plastics | Nylon 6 | Starflam |
| TOTAL Polyethylene XSene® HDPE XS 10 Orange YCF | TOTAL Refining & Chemicals | HDPE | TOTAL Polyethylene |
| Ferro PP LPP10YE09BK | Ferro Corporation | PP Homopolymer | Ferro PP |
| FireCon™ CPE 0883-01 RoHS BLACK | PolyOne Corporation | CPE | FireCon™ |
| DynaMix Lite™ 2244-GHI | Polymer Dynamix | Nylon 12 | DynaMix Lite™ |