Descriptions: DESTRON™ DSC1701GH7 is semi-crystalline PPA(Polyphthalamide) Glass fiber 35% reinforced grade. It has great mechanical properties, good dimensional stability and excellent thermal performance. Applications: DESTRON™ DSC1701GH7 is applicable for automotive industry, water handling, telecommunications and several industrial equipment. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.48 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.40 - 0.80 | % | |
| Water Absorption (23°C, 24 hr) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 125 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 221 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.6 | % | ASTM D638 |
| Flexural Modulus | 11800 | MPa | ASTM D790 |
| Flexural Strength | 294 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 300 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 285 | °C | ASTM D648 |
| Melting Temperature | 310 | °C | DSC |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 22 | kV/mm | ASTM D149 |
| Arc Resistance | 140 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 135 | °C | |
| Drying Time | 4.0 - 5.0 | hr | |
| Rear Temperature | 310 - 320 | °C | |
| Middle Temperature | 315 - 345 | °C | |
| Front Temperature | 320 - 345 | °C | |
| Nozzle Temperature | 320 - 345 | °C | |
| Processing (Melt) Temp | 320 - 345 | °C | |
| Mold Temperature | 100 - 140 | °C |
| Injection instructions |
|---|
| Speed: 40 to 70%Pressure 1st: 30 to 60%Pressure 2nd: 30 to 60Holding Pressure: 10 to 20% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reny® 1021UCS | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| Sylvin 7842-75 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| AMTOPP CE18 | Inteplast Group | PP, Unspecified | AMTOPP |
| Hifax EKC 177P | LyondellBasell Industries | PP Copolymer | Hifax |
| Hiprolon® 200 MNNHL G15 | Arkema | Nylon 1010 | Hiprolon® |