3M™ Dyneon™ Fluoroplastic PVDF 31508/0009
| Category: | PVDF , Polyvinylidene Fluoride |
| Manufacturer: | 3M Advanced Materials Division |
| Trademark: | 3M™ Dyneon™ Fluoroplastic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hFRzFD_3M-Dyneon-Fluoroplastic-PVDF-31508-0009.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
3M™ Dyneon™ Fluoroplastic PVDF 31508/0009 is a Polyvinylidene Fluoride (PVDF) product. It can be processed by extrusion and is available in Europe or North America. Applications of 3M™ Dyneon™ Fluoroplastic PVDF 31508/0009 include wire & cable and hose/tubing. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.76 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 230°C/2.16 kg | 5.0 | g/10 min | |
| 230°C/5.0 kg | 15 | g/10 min | |
| Water Absorption 1(23°C, 24 hr) | < 0.040 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Break, 23°C) | 22.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, 23°C) | 480 | % | ASTM D638 |
| Flexural Modulus 4(23°C) | 425 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -37.0 | °C | ASTM D746A |
| Peak Melting Temperature | 169 | °C | ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 5 | > 1.0E+14 | ohms | ASTM D257 |
| Volume Resistivity 6 | > 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Constant (1 MHz) | 7.00 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 | |
| Oxygen Index (3.00 mm) | 100 | % | ASTM D2863 |
| Note Message | |
|---|---|
| 1 . | Method 1 |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | Voltage <1V, after 2 min - 500V |
| 6 . | Intensity = 10mA, after 2 min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REPOL® B220MN | Reliance Industries Limited | PP Impact Copolymer | REPOL® |
| Fainplast PVC RK 740/OM | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| ICORENE® N1016 | ICO Polymers EMEA, A Division of A. Schulman | EVA | ICORENE® |
| Karina STRAW PVC COMPOUND 828-38/ 98-AY-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| POCAN® KU 2-7241 000000 | LANXESS GmbH | PBT | POCAN® |