Message
MDF603 is a 15% glass fibre reinforced, impact modified nylon 6 that offers good rigidity and toughness over a wide temperature range.

General Information
Filler / Reinforcement	Glass fiber reinforced material, 15% filler by weight
Additive	Impact modifier
Features	Impact modification Good toughness Medium hardness
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.20	g/cm³	ISO 1183
Molding Shrinkage ¹	0.80 - 1.6	%	Internal method
Water Absorption (Equilibrium, 23°C, 50% RH)	2.2	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	4400	MPa	ISO 527-2
Tensile Stress	90.0	MPa	ISO 527-2
Tensile Strain (Break)	9.0	%	ISO 527-2
Flexural Modulus	3600	MPa	ISO 178
Flexural Stress	110	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength	15	kJ/m²	ISO 179/1eA
Notched Izod Impact	12	kJ/m²	ISO 180/A
Unnotched Izod Impact Strength	> 45	kJ/m²	ISO 180

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	200	°C	ISO 75-2/B
1.8 MPa, not annealed	190	°C	ISO 75-2/A

Flammability	Nominal Value		Test Method
Flame Rating (1.50 mm, Teknor Apex test result)	HB		UL 94

Injection	Nominal Value	Unit
Drying Temperature	80.0	°C
Drying Time	20	hr
Rear Temperature	250 - 280	°C
Middle Temperature	250 - 280	°C
Front Temperature	250 - 280	°C
Processing (Melt) Temp	250 - 290	°C
Mold Temperature	60.0 - 80.0	°C
Injection Rate	Fast
Back Pressure	Moderate
Screw Speed	Moderate

Injection instructions
No drying is necessary unless the material has been exposed to air for longer than three hours. The appearance of splash marks on the surface of mouldings indicates excessive moisture is present.

Note Message
1 .	Mould shrinkage is significantly influenced by many factors including wall thickness, gating, moulding shape and processing conditions. The range values given are determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding).

Note Message

1 .

Mould shrinkage is significantly influenced by many factors including wall thickness, gating, moulding shape and processing conditions. The range values given are determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding).

Category:	Nylon 6 , Polyamide 6
Manufacturer:	Teknor Apex Company (Chem Polymer)
Trademark:	Chemlon®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	hFG12t_Chemlon-MDF603.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
RTP 4702 TFE 15 SI 2	RTP Company	PTT	RTP
Teflon® PTFE 62N X	DuPont Fluoropolymers	PTFE	Teflon® PTFE
TEREZ PMMA 5605 SZ	TER HELL PLASTIC GMBH	Acrylic (PMMA)	TEREZ PMMA
Beamset 255	Arakawa Chemical Industries, Ltd.	Acrylic, Unspecified	Beamset
POLYblend PC/ABS 45FS GF20	Polykemi AB	PC+ABS	POLYblend