LNP™ LUBRICOMP™ PFP36 compound
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hF1mR4_LNP-LUBRICOMP-PFP36-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP PFL36 is a compound based on Nylon 6 resin containing 30% Glass Fiber, 15% PTFE/Silicone. Added features of this grade include: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound PFL-4536 Product reorder name: PFP36 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.22 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (24 hr) | 1.2 to 1.4 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3200 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 55.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 6.0 to 8.0 | % | ISO 527-2 |
| Flexural Modulus | 3100 | MPa | ISO 178 |
| Flexural Stress | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 1(23°C) | 8.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 2(23°C) | 100 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3(1.8 MPa, Unannealed, 64.0 mm Span) | 58.0 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 243 to 254 | °C | |
| Middle Temperature | 249 to 260 | °C | |
| Front Temperature | 249 to 260 | °C | |
| Processing (Melt) Temp | 254 to 266 | °C | |
| Mold Temperature | 54.4 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 80*10*4 |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MALAT 38GFRH300 | AD majoris | PBT | MALAT |
| Advanced Composites ATX639MX2N | Advanced Composites, Inc. | PP, Unspecified | Advanced Composites |
| GERMAMID 6.6 CF 12-7163 | Kunststoff-Kontor-Hamburg GmbH | Nylon 66 | GERMAMID |
| Hapflex™ 666-3 | Hapco Inc. | TP, Unspecified | Hapflex™ |
| LNP™ LUBRICOMP™ QCL34 compound | SABIC Innovative Plastics | Nylon 610 | LNP™ LUBRICOMP™ |