Order Products : sales@su-jiao.com
PPR POM02
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Premier Plastic Resins, Inc. |
| Trademark: | PPR |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hDtSgD_PPR-POM02.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Acetal Copolymer Black |
| General Information | |
|---|---|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 9.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 2.2 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 60.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 65 | % | ASTM D638 |
| Flexural Modulus - Tangent | 2590 | MPa | ASTM D790 |
| Flexural Strength | 91.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 70 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 160 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 110 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 77.0 - 88.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 188 - 221 | °C | |
| Middle Temperature | 185 - 216 | °C | |
| Front Temperature | 185 - 216 | °C | |
| Nozzle Temperature | 193 - 210 | °C | |
| Processing (Melt) Temp | 199 - 227 | °C | |
| Mold Temperature | 82.0 - 104 | °C | |
| Injection Pressure | 69.0 - 110 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 41.0 - 83.0 | MPa | |
| Back Pressure | 0.00 | MPa | |
| Cushion | 6.35 - 12.7 | mm |
| Injection instructions |
|---|
| Screw Speed: ModerateDecompression: 3.81 to 7.6 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 F TFE 20 SI | RTP Company | Nylon 12 | RTP |
| Prime Polypro™ J-2041GA | Prime Polymer Co., Ltd. | PP Random Copolymer | Prime Polypro™ |
| Stanyl® TS250FK33 | DSM Engineering Plastics | Nylon 46 | Stanyl® |
| Trexprene® D40BU | Mitsubishi Chemical Performance Polymers, Inc. | TPV | Trexprene® |
| Plaslube® PA6/6 GF60 TL10 | Techmer Engineered Solutions | Nylon 66 | Plaslube® |