LNP™ LUBRICOMP™ AG5LT2 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hDA8Vi_LNP-LUBRICOMP-AG5LT2-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* LUBRICOMP* AG5LT2 Is a compound based on PA66 resin, containing Glass Fiber and PTFE. Added features include: Internally Lubricated Also known as: LNP* LUBRICOMP* Compound AG5LT2 Product reorder name: AG5LT2 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.40 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.20 to 0.40 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.74 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 168 | MPa | ISO 527-2/5 |
| Tensile Strain (Yield) | 3.4 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 7900 | MPa | ISO 178 |
| Flexural Stress | 234 | MPa | ISO 178 |
| Coefficient of Friction (vs. Itself - Dynamic) | 0.42 | ASTM D3702 Modified | |
| Flexural Strain at Break 2 | 3.7 | % | ISO 178 |
| Wear Factor - Washer | 11.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 3(23°C) | 11 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 4(23°C) | 55 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 259 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 246 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 2.5E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 9.9E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 6 GF 35 H BLACK REC | A. Schulman Europe | Nylon 6 | SCHULAMID® |
| BCC Resins BC 8690E | BCC Products Inc. | TSU | BCC Resins |
| ARCEL® ULV (2.00 pcf) | NOVA Chemicals | PS+PE | ARCEL® |
| DILAMID® 66 FV 15 NATURAL | Dilaplast S.p.A. | Nylon 66 | DILAMID® |
| Karina GREEN PVC COMPOUND -E 870-40/511-A-IS (C850) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |