Radilon® CS 38FL
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | Radici Plastics |
| Trademark: | Radilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hByrxI_Radilon-CS-38FL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA6/66 medium-high viscosity extrusion grade for cast, blown and co-extruded films and monofilaments. Natural colour. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.14 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 10 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 3.0 | -- | % | ISO 62 |
| Viscosity Number | 230 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2800 | 750 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 80.0 | 29.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 4.2 | 17 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 50 | 50 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/eA | |||
| -30°C | 5.3 | -- | kJ/m² | ISO 179/eA |
| 23°C | 5.5 | 130 | kJ/m² | ISO 179/eA |
| Charpy Unnotched Impact Strength | ISO 179/eU | |||
| -30°C | No Break | -- | ISO 179/eU | |
| 23°C | No Break | No Break | ISO 179/eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 70.0 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 65.0 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 70.0 | -- | °C | ISO 306/B50 |
| Melting Temperature (DSC) | 210 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | -- | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | 1.0E+13 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | -- | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | HB | -- | UL 94 | |
| 1.60 mm | HB | -- | UL 94 |
| Additional Information |
|---|
| 干燥 The value listed as Melting Temperature, ISO 3146, was tested in accordance with ISO 11357-1-3 at a heating rate of 10°C/min.Nominal Tensile Strain at Break, ISO 527: >50% |
| 调节后的 Nominal Tensile Strain at Break, ISO 527: >50% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer FE-381U | Shin-Etsu Silicones of America | Fluoro Si | Shin-Etsu Elastomer |
| Celcon® LW90-S2 | Celanese Corporation | Acetal (POM) Copolymer | Celcon® |
| Ferro PP TPP40AC86BK | Ferro Corporation | PP Homopolymer | Ferro PP |
| Flontech® FT-1-GRN | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Kinta NB2630G | Kinta Technology (Hong Kong) Co., Ltd. | PP, Unspecified | Kinta |