CALIBRE™ 303-22
| Category: | PC , Polycarbonate Resin |
| Manufacturer: | Trinseo |
| Trademark: | CALIBRE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hBqIRK_CALIBRE-303-22.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CALIBRE™ 303-22 SC830104 Opalescent Polycarbonate Resin offers exceptional impact resistance, heat distortion resistance, and opalescence for injection molding applications. The high melt flow rate allows complex parts to be easily molded. The resin is UV stabilized and contains mould release agent . Govt. and Industry Standards:
Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183/B |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 22 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.15 | % | |
| Equilibrium, 23°C, 50% RH | 0.32 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ISO 2039-2 | ||
| M-Scale | 73 | ||
| R-Scale | 118 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2/50 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 60.0 | MPa | |
| Break | 65.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 6.0 | % | |
| Break | 120 | % | |
| Flexural Modulus 1 | 2400 | MPa | ISO 178 |
| Flexural Stress 2 | 97.0 | MPa | ISO 178 |
| Taber Abrasion Resistance | 45 | % | ASTM D1044 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| a* | |||
| 1.00 mm | 0.0100 | ||
| 2.00 mm | 0.140 | ||
| 3.00 mm | 0.360 | ||
| b* | |||
| 1.00 mm | 1.63 | ||
| 2.00 mm | 3.14 | ||
| 3.00 mm | 4.34 | ||
| Diffusivity | |||
| 1.00 mm | 78 | ||
| 2.00 mm | 68 | ||
| 3.00 mm | 58 | ||
| L* | |||
| 1.00 mm | 91.5 | ||
| 2.00 mm | 87.8 | ||
| 3.00 mm | 83.4 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 20 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact Strength (23°C) | 74 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Annealed | 142 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 122 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed | 139 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 147 | °C | ISO 306/B50 |
| Ball Indentation Temperature | > 125 | °C | IEC 60598-1 |
| CLTE - Flow | 6.8E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 17 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 60 Hz | 3.00 | IEC 60250 | |
| 1 MHz | 3.00 | IEC 60250 | |
| 100 Hz | 3.00 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 1.0E-3 | ||
| 1 MHz | 2.0E-3 | ||
| Comparative Tracking Index (2.00 mm, Solution A) | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 3 | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB | ||
| Glow Wire Flammability Index 4 | IEC 60695-2-12 | ||
| 1.00 mm | 900 | °C | |
| 2.00 mm | 875 | °C | |
| 3.00 mm | 875 | °C | |
| Glow Wire Ignition Temperature 5 | IEC 60695-2-13 | ||
| 1.00 mm | 800 | °C | |
| 2.00 mm | 775 | °C | |
| 3.00 mm | 775 | °C | |
| Oxygen Index 6 | 26 | % | ISO 4589-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | |||
| 1000 µm | 79.6 | % | |
| 2000 µm | 71.6 | % | |
| 3000 µm | 62.9 | % | |
| Haze | |||
| 1000 µm | 79 | % | |
| 2000 µm | 92 | % | |
| 3000 µm | 96 | % | |
| Yellowness Index | ASTM D1925 | ||
| 1.00 mm | 3.0 | YI | |
| 2.00 mm | 6.1 | YI | |
| 3.00 mm | 8.9 | YI |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 4 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 5 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 6 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECDUR® B DF 30 SCHWARZ-14345 | LEIS Polytechnik - polymere Werkstoffe GmbH | PBT+ASA | TECDUR® |
| FHR Polypropylene P4C5B-076 | Flint Hills Resources, LP | PP Homopolymer | FHR Polypropylene |
| Hifax BA45H | LyondellBasell Industries | PP Copolymer | Hifax |
| Hostacom X M3 T16 100000 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Rotuba CAB B902 (16% Plasticizer) | Rotuba Extruders, Inc. | CAB | Rotuba CAB |