Order Products : sales@su-jiao.com
Estane® ZHF 90AT2 TPU
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Estane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hBZL8p_Estane-ZHF-90AT2-TPU.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Type: Estane® ZHF90AT2 NAT 022 is a halogen free, flame retardant, aromatic polyether-based thermoplastic polyurethane. Appearance: White opaque spherical pellets Application: Cable & Wire Features: Zero halogen |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ISO 2781 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 1 sec) | 90 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Resistance | 38.0 | mm³ | ISO 4649-A |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-3/5/200 | ||
| Fracture | 28.0 | MPa | ISO 527-3/5/200 |
| 50% strain | 8.00 | MPa | ISO 527-3/5/200 |
| 100% strain | 9.00 | MPa | ISO 527-3/5/200 |
| 300% strain | 13.7 | MPa | ISO 527-3/5/200 |
| Tensile Elongation (Break) | 520 | % | ISO 527-3/5/200 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 1 | 85 | kN/m | ISO 34-1 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 85.0 | °C | ISO 306/A50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | V-2 | UL 94 | |
| Oxygen Index | 24 | % | ASTM D2863 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Cylinder Zone 1 Temp. | 200 | °C | |
| Cylinder Zone 2 Temp. | 205 | °C | |
| Cylinder Zone 3 Temp. | 210 | °C | |
| Cylinder Zone 4 Temp. | 205 | °C | |
| Adapter Temperature | 205 | °C | |
| Die Temperature | 205 | °C |
| Extrusion instructions |
|---|
| L/D Ratio: 25:1Compression Ratio: 3:1Dew Point: -30°C to -40°CDie Tip: 200°C |
| Note Message | |
|---|---|
| 1 . | Method B, right-angle specimen (cut) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom PP7150 | Spartech Polycom | PP Copolymer | Spartech |
| Tufel® II 94406 | Momentive Performance Materials Inc. | Silicone | Tufel® II |
| Ultramid® B3ZG3 | BASF Corporation | Nylon 6 | Ultramid® |
| Network Polymers PP PPB 25 0620 | Network Polymers, Inc. | PP Copolymer | Network Polymers PP |
| Arnite® TV4 260 SXF | DSM Engineering Plastics | PBT | Arnite® |