WPP PP PPC3GF1.5-Black
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Washington Penn Plastic Co. Inc. |
| Trademark: | WPP PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hB5XGW_WPP-PP-PPC3GF1-5-Black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Properties shown below for this filled blend are typical for a15% fiberglass reinforced polypropylene copolymer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.982 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 33.8 | MPa | ASTM D638 |
| Flexural Modulus 2 | 1570 | MPa | ASTM D790 |
| Flexural Strength 3 | 46.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 210 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 147 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 87.0 | °C | ASTM D648 |
| Additional Information |
|---|
| Tested at 23 ± 2°C (73.4 ± 3.6°F) and 50 ± 5% relativehumidity unless otherwise noted |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 5.3 mm/min |
| 3 . | 5.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Huafon JF-PDY-511H | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| Huafon JF-P-5675 / JF-I-5118 | Huafon Group Co., Ltd. | PUR-Ester | Huafon |
| Osterlene® HI-8-2-hg | Osterman & Company | PS (HIPS) | Osterlene® |
| Pinnacle PP 1350N | Pinnacle Polymers | PP Homopolymer | Pinnacle PP |
| Moplen HP522H | LyondellBasell Industries | PP Homopolymer | Moplen |