Ecolac F17 NERO
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Soredi S.p.a. |
| Trademark: | Ecolac |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hALGK4_Ecolac-F17-NERO.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ABS reinforced with 17% glass fibre. Industrial quality |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.20 - 0.40 | % | ASTM D955 |
| Transverse flow | 0.30 - 0.50 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.20 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 55.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus 3 | 4500 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 50 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 100 | °C | ASTM D1525 4 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | UL 94 | |
| 3.20 mm | HB | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 650 | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| Melt Mass- Flow Rate (MFR), ASTM D1238, 220°C/10kg: 5 to 15 g/10min |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RANPELEN J-580S | Lotte Chemical Corporation | PP Random Copolymer | RANPELEN |
| STERalloy™ FDG 2056-5 | Hapco Inc. | TP, Unspecified | STERalloy™ FDG |
| Hifax TYC 1123P E C11538 | LyondellBasell Industries | PP Copolymer | Hifax |
| Kumho KNB 25H | Korea Kumho Petrochemical Co., Ltd. | NBR | Kumho KNB |
| InnoGreen® BIO-80D | Innovative Polymers, Inc. | TSU | InnoGreen® |