Elastocon® STK60

Category:	TPE , Thermoplastic Elastomer
Manufacturer:	Elastocon TPE Technologies
Trademark:	Elastocon®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	h8xXBa_Elastocon-STK60.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Elastocon® STK60 thermoplastic elastomer has been developed for applications that require ultra soft rubber-like properties and a good surface finish. Elastocon® STK60 is FDA compliant and well suited for consumer goods and industrial applications requiring non-slip/soft touch ergonomics, sound and vibration dampening, improved impact resistance, and U.V. stability. Elastocon® STK60 can be overmolded to polycarbonate, ABS, PC/ABS, Acrylic, HIPS, and various grades of nylon 6 and 6/6.

General Information
Features	Shock absorption Noise reduction Impact resistance, good Good UV resistance Soft Excellent appearance
Uses	overmolding Industrial application Consumer goods application field
Forms	Particle
Processing Method	Blow molding Extrusion Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.920	g/cm³	ASTM D792

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A)	64		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress (100% Strain)	2.04	MPa	ASTM D412
Tensile Strength (Yield)	5.37	MPa	ASTM D412
Tensile Elongation (Break)	570	%	ASTM D412

Injection	Nominal Value	Unit
Rear Temperature	210 - 216	°C
Front Temperature	216 - 266	°C
Nozzle Temperature	227 - 277	°C
Mold Temperature	27.0 - 49.0	°C
Back Pressure	0.520 - 1.21	MPa

Injection instructions
Elastocon® thermoplastic elastomers are shear dependent and have been formulated to process on conventional thermoplastic equipment for injection molding, extrusion or blow molding. Our tests have shown that overmolding onto a non-gloss, matte surface finish will help optimize overmold adhesion to the substrate. Be sure to incorporate mechanical interlocks and 1:1 through holes whenever possible when designing two shot components. Feathered edges should always be avoided to ensure adequate and consistant shut off against the substrate, while also eliminating exposed tapered edges that can be subject to adhesive failure.Injection Rate: 1 to 5 in/sec

Injection instructions

Elastocon® thermoplastic elastomers are shear dependent and have been formulated to process on conventional thermoplastic equipment for injection molding, extrusion or blow molding. Our tests have shown that overmolding onto a non-gloss, matte surface finish will help optimize overmold adhesion to the substrate. Be sure to incorporate mechanical interlocks and 1:1 through holes whenever possible when designing two shot components. Feathered edges should always be avoided to ensure adequate and consistant shut off against the substrate, while also eliminating exposed tapered edges that can be subject to adhesive failure.Injection Rate: 1 to 5 in/sec

Resin Grade	Manufacturer	Category	Trademark
RTP 2200 LF AR 15 TFE 10	RTP Company	PEEK	RTP
Pro-fax SC204	LyondellBasell Industries	PP Impact Copolymer	Pro-fax
DJSilicone NE-9250	DONGJUE SILICONE (NANJING) CO., LTD	Silicone	DJSilicone
Generic SBR, Emulsion	Generic	SBR, Emulsion	Generic
Karina CLEAR PVC COMPOUND 80/275-IS-RG	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina