Latene® AG7H2 G/50
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | h7lPrF_Latene-AG7H2-G-50.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polypropylene homopolymer (PPh). Chemically coupled fibers. Heat stabilised. Glass fibres. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.32 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.75 to 1.1 | % | |
| Flow : 2.00 mm | 0.25 to 0.50 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 10000 | MPa | |
| 60°C | 8200 | MPa | |
| 90°C | 5300 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 60°C | 65.0 | MPa | |
| Yield, 90°C | 40.0 | MPa | |
| Break, 23°C | 105 | MPa | |
| Break, 60°C | 65.0 | MPa | |
| Break, 90°C | 40.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 60°C | 2.7 | % | |
| Yield, 90°C | 4.2 | % | |
| Break, 23°C | 2.5 | % | |
| Break, 60°C | 3.4 | % | |
| Break, 90°C | 6.0 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 4.0 | kJ/m² | |
| 23°C | 5.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 18 | kJ/m² | |
| 23°C | 20 | kJ/m² | |
| Notched Izod Impact (23°C, 3.20 mm) | 60 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 160 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 140 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 125 | °C | |
| Vicat Softening Temperature | 140 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 8.0E-6 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 200 to 240 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® HT CMNO | Arkema | PPA | Rilsan® HT |
| Starex SR-0325LTS | SAMSUNG SDI CO., LTD. | ABS | Starex |
| Novodur® H701 | Styrolution | ABS | Novodur® |
| NILAMID® XT1 GF50 | Nilit Plastics | PPA | NILAMID® |
| LNP™ VERTON™ MX02795 compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ VERTON™ |