Andur 9500-AP/Curene® 280
| Category: | PUR-Ether/TDI , Polyurethane (Polyether, TDI) |
| Manufacturer: | Anderson Development Company |
| Trademark: | Andur |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | h68FYS_Andur-9500-AP-Curene-280.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| All properties based on Andur® 9500-AP cured with Curene® 280 |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness (Shore A) | 82 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 16.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 400 | % | ASTM D638 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 4.83 | MPa | ASTM D412 |
| 300% strain | 10.0 | MPa | ASTM D412 |
| Tear Strength | |||
| -- 1 | 45.5 | kN/m | ASTM D624 |
| Cracking | 9.6 | kN/m | ASTM D470 |
| Compression Set | 29 | % | ASTM D395 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Pot Life | 6.0 | min | |
| Post Cure Time (23°C) | 72 | hr |
| Additional Information |
|---|
| Prepolymer NCO%: 5.8-6.2Grams Curene® 280 per 100 grams prepolymer: 38.0Rebound, %: 30Stoichiometry: 0.95Prepolymer Temperature, °F: 190-210Curene® 280 Temperature, °F: 158Post Cure Time, 212°F, hours: 16 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 107 | °C |
| Note Message | |
|---|---|
| 1 . | C mould |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ranger PBT PBT-201-G25 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| Vi-Chem PVC V221-60E | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| DJSilicone NE-Z250 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| Flontech® FT-M01-1 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| LNP™ THERMOCOMP™ RF008ESY compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |