Styroflex® 2G66
| Category: | SBC , Styrene Butadiene Block Copolymer |
| Manufacturer: | INEOS Styrolution Group GmbH |
| Trademark: | Styroflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | h5LhWE_Styroflex2G66.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Styroflex® 2G66 is a styrene-butadiene block copolymer (SBC) with the properties of a thermoplastic elastomer (S-TPE) suitable for extrusion (blown and cast film) and for injection molding. Styroflex® 2G66 is also used for polymers modification and compatibilization. It is more polar than comparable SBS or SEBS grades and offers a combination of high resilience and toughness with good transparency and process stability. FEATURES
APPLICATIONS
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.999 | g/cm³ | ASTM D792 |
| -- | 1.00 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 11 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (200°C/5.0 kg) | 13.0 | cm³/10min | ISO 1133 |
| Water Absorption (Saturation, 23°C) | 0.070 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | |||
| Shaw A | 91 | ASTM D2240 | |
| Shaw D | 36 | ASTM D2240 | |
| Shaw A | 84 | ISO 868 | |
| Shaw D | 34 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- | 128 | MPa | ASTM D638 |
| -- | 120 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 3.10 | MPa | ASTM D638 |
| Yield, 23°C | 4.00 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 5.0 | % | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | > 500 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 82.7 | MPa | ASTM D790 |
| -- | 140 | MPa | ISO 178 |
| Flexural Strength | |||
| 5.0% strain | 2.70 | MPa | ASTM D790 |
| -- | 4.00 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Elastic Modulus - MD | 170 | MPa | ASTM D882 |
| Elastic Modulus - TD | 128 | MPa | ASTM D882 |
| Tensile Elongation | |||
| MD : Fracture | 550 | % | ASTM D882 |
| TD : Fracture | 540 | % | ASTM D882 |
| MD : Fracture | > 500 | % | ISO 527-3 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 530 | g | ASTM D1922 |
| TD | 540 | g | ASTM D1922 |
| Oxygen Transmission Rate (23°C, 0% RH) | 86000 | cm³/m²/24 hr | ASTM D3985 |
| Water Vapor Transmission Rate 1(23°C) | 150 | g/m²/24 hr | ASTM F1249 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 2.0 | kJ/m² | ISO 179 |
| 23°C | No Break | ISO 179 | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ISO 179 | |
| 23°C | No Break | ISO 179 | |
| Notched Izod Impact (23°C) | No Break | ASTM D256 | |
| Instrumented Dart Impact | ASTM D3763 | ||
| Peak force | 2.41 | J | ASTM D3763 |
| Total energy | 3.41 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 47.8 | °C | ASTM D1525 2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257, IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Constant (100 Hz) | 2.50 | IEC 60250 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index 3 | 1.565 | ASTM D542, ISO 489 | |
| Transmittance (550 nm) | 93.0 | % | ASTM D1003 |
| Haze | 1.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 170 - 240 | °C | |
| Mold Temperature | 30 - 50 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 170 - 240 | °C |
| Note Message | |
|---|---|
| 1 . | 0% to 85% RH gradient |
| 2 . | 标准 B (120°C/h), 压 力1 (10N) |
| 3 . | Sodium D Line |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEO-ZEX™ 3510F | Prime Polymer Co., Ltd. | LLDPE | NEO-ZEX™ |
| Novalloy-S S1500 | PlastxWorld Inc. | PC+ABS | Novalloy-S |
| ECOGRAN® PPCI F20 BLK | Eurocompound Polymers | PP Copolymer | ECOGRAN® |
| Karina WHITE PVC COMPOUND -E 855-10/150-ERYB-PO | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| POCAN® B 1305 000000 | LANXESS GmbH | PBT | POCAN® |