GAPEX® RPP40EA59HB BLACK
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Ferro Corporation |
| Trademark: | GAPEX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | h4wBEI_GAPEX-RPP40EA59HB-BLACK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| GAPEX®RPP40EA59HB BLACK is a polypropylene homopolymer (PP Homopoly) material, which contains a 43% glass fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. GAPEX®The main characteristics of RPP40EA59HB BLACK are: chemical coupling. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.26 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.20 | % | ASTM D955 |
| Transverse flow | 1.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 89.6 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 4.0 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% secant : 23°C | 7580 | MPa | ASTM D790 |
| Tangent : 23°C | 8270 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 138 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 160 | °C | ASTM D648 |
| Additional Information |
|---|
| Testing and measurements were performed at 73 +/-3°F and 50 +/-5% relative humidity unless otherwise noted. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 82.2 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 221 - 238 | °C | |
| Middle Temperature | 227 - 243 | °C | |
| Front Temperature | 232 - 260 | °C | |
| Nozzle Temperature | 232 - 260 | °C | |
| Processing (Melt) Temp | 221 - 238 | °C | |
| Mold Temperature | 37.8 - 65.6 | °C | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 0.138 - 0.345 | MPa | |
| Cushion | 5.08 - 12.7 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultramid® T 4381 LDS | BASF Corporation | Nylon 6/6T | Ultramid® |
| NEOFLON™ NP-130 | DAIKIN AMERICA, INC. | FEP | NEOFLON™ |
| Cellophane™ XS365 | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| ALTECH® PA66 ECO 2033/509 GF33 | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |
| Sylvin 9812-65 Orange 594 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |