Generic Nylon 610
| Category: | Nylon 610 , Polyamide 610 |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | h4T714_Generic-Nylon-610.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Nylon 610 This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.07 - 1.08 | g/cm³ | ASTM D792 |
| 23°C | 1.03 - 1.09 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.28 - 2.5 | % | ASTM D955 |
| 23°C | 0.87 - 1.6 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.26 - 1.4 | % | ASTM D570 |
| Saturated, 23°C | 1.8 - 4.0 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.37 - 1.7 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 35.0 - 130 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 2140 - 2800 | MPa | ASTM D638 |
| 23°C | 450 - 6470 | MPa | ISO 527-2 |
| Tensile Stress | |||
| Yield, 23°C | 34.9 - 65.3 | MPa | ISO 527-2 |
| Fracture, 23°C | 30.9 - 111 | MPa | ISO 527-2 |
| 23°C | 51.7 - 70.3 | MPa | ASTM D638 |
| Tensile Strain | |||
| Yield, 23°C | 4.5 - 6.9 | % | ISO 527-2 |
| Fracture, 23°C | 2.4 - 300 | % | ASTM D638 |
| Fracture, 23°C | 3.0 - 54 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 1300 - 2280 | MPa | ASTM D790 |
| 23°C | 530 - 2060 | MPa | ISO 178 |
| Flexural Stress (23°C) | 22.0 - 95.7 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 - 18 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 80 - 100 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 35 - 200 | J/m | ASTM D256 |
| 23°C | 4.1 - 80 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 160 - 175 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 115 - 180 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 59.8 - 66.3 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 50.0 - 201 | °C | ISO 75-2/A |
| Continuous Use Temperature | 113 - 160 | °C | ASTM D794 |
| Melting Temperature | 215 - 225 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 2.0E-5 - 2.0E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral | 8.0E-5 - 1.5E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+10 - 2.5E+14 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+11 - 1.5E+12 | ohms·cm | IEC 60093 |
| Dielectric Strength (23°C) | 30 - 45 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 599 - 600 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.3 - 82.2 | °C | |
| Drying Time | 2.0 - 5.0 | hr | |
| Suggested Max Moisture | 0.10 - 0.20 | % | |
| Rear Temperature | 216 - 254 | °C | |
| Middle Temperature | 221 - 266 | °C | |
| Front Temperature | 227 - 277 | °C | |
| Processing (Melt) Temp | 248 - 288 | °C | |
| Mold Temperature | 50.9 - 87.8 | °C | |
| Injection Pressure | 8.62 - 10.8 | MPa | |
| Back Pressure | 0.258 - 0.689 | MPa |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Nylon 610This information is provided for comparative purposes only. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Moisture | 0.099 - 0.10 | % |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Nylon 610This information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumikon® PM-9501 (Injection) | Sumitomo Bakelite North America, Inc. | Phenolic | Sumikon® |
| Viprene™ G55A-32U-BLK | Alliance Polymers & Services | TPV | Viprene™ |
| Ferro PP NPP00GW13HB | Ferro Corporation | PP, Unspecified | Ferro PP |
| TECHNYL® A 218 BLACK 21N | Solvay Engineering Plastics | Nylon 66 | TECHNYL® |
| LEXAN™ 923A resin | SABIC Innovative Plastics | PC | LEXAN™ |