RTP 1407
| Category: | PESU , Polyethersulfone |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | h1Agtl_RTP-1407.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass Fiber |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.68 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.10 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ASTM D570 |
| Moisture Content | 0.040 | % |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Primary Additive | 40 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 123 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 12400 | MPa | ASTM D638 |
| Tensile Strength | 159 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 2.1 | % | ASTM D638 |
| Flexural Modulus | 11700 | MPa | ASTM D790 |
| Flexural Strength | 224 | MPa | ASTM D790 |
| Compressive Strength | 152 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 96 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 670 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 221 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 216 | °C | ASTM D648 |
| CLTE - Flow | 2.5E-5 | cm/cm/°C | ASTM E831 |
| Thermal Conductivity 1 | 0.36 | W/m/K | ASTM E1530 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+12 | ohms·cm | ASTM D257 |
| Dielectric Strength 2(in Oil) | 15 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 4.30 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 7.0E-3 | ASTM D150 | |
| Arc Resistance | 80.0 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, ** Values per RTP Company testing.) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 6.0 | hr | |
| Dew Point | -31.7 | °C | |
| Processing (Melt) Temp | 343 - 377 | °C | |
| Mold Temperature | 135 - 177 | °C | |
| Injection Pressure | 68.9 - 103 | MPa |
| Injection instructions |
|---|
| Desiccant Type Dryer Required. |
| Note Message | |
|---|---|
| 1 . | Through-plane |
| 2 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUMIPEX® HT03Y | Sumitomo Chemical Co., Ltd. | Acrylic (PMMA) | SUMIPEX® |
| Sunny® PC-PBT EN120 | Guangdong Shunde Shunyan New Material Co., Ltd. | PC+PBT | Sunny® |
| Escorene™ Ultra FL 00226CC | ExxonMobil Chemical | EVA | Escorene™ Ultra |
| PENTAMID A GV40 H natural | PENTAC Polymer GmbH | Nylon 66 | PENTAMID A |
| Crastin® FR1300TC BK350 | DuPont Performance Polymers | PBT | Crastin® |