BCC Resins BC 7136
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | BCC Products Inc. |
| Trademark: | BCC Resins |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | h1474Z_BCC-Resins-BC-7136.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| BC 7136 is a gray, low toxicity, aluminum filled, epoxy casting resin. This heat resistant system may be used at room temperature without post-curing. May be cast to a thickness of ¾ inch in non-conductive molds. For use above 150°F a post-cure is required. Post cure for applications requiring temperatures above 150°F can be accomplished in an oven or in use by a gradual heat rise; 2 hours @ 150°F, plus 2 hours @ 250°F, plus 2 hours at 300°F. BC 7136 can afford consistent use to 300°F if required. This product was engineered to replace VCHD and MDA systems while retaining excellent heat resistance and low viscosity. Typical uses include constructing vacuum form tools, Injection and compression molds, RTM and RIM molds, and matched dies. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.69 | g/cm³ | ASTM D792, ASTM D1505 |
| Molding Shrinkage - Flow | 0.11 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 90 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Ultimate) | 53.8 | MPa | ASTM D638 |
| Flexural Strength (Break) | 59.3 | MPa | ASTM D790 |
| Compressive Strength | 200 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 152 | °C | ASTM D648 |
| CLTE - Flow | 3.4E-5 | cm/cm/°C | ASTM D696 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 7.0, Mix Ratio by Volume: 12 | ||
| Resin | Mix Ratio by Weight: 100, Mix Ratio by Volume: 100 | ||
| Pot Life (24°C) | 85 | min | |
| Thermoset Mix Viscosity (24°C) | 15000 | cP | ASTM D2393 |
| Demold Time | 1400 | min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYFORT® FPP 40 GFC HI | A. Schulman Europe | PP Homopolymer | POLYFORT® |
| ResMart Repro CoPP 10 | ResMart | PP Impact Copolymer | ResMart Repro |
| Shandong PP PF01 | Shandong Dongchen Engineering Plastics Co., Ltd. | PP, Unspecified | Shandong PP |
| Spartech Polycom PP7140 | Spartech Polycom | PP Copolymer | Spartech |
| Sylvin 8479-90 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |