UmaPET HCM
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Ester Industries Ltd. |
| Trademark: | UmaPET |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gyZi63_UmaPET-HCM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
KEY FEATURES
APPLICATIONS
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage | ASTM D1204 | ||
| Flow : 150°C, 30 min, 0.0120 mm | 2.5 | % | |
| Flow : 150°C, 30 min, 0.0150 mm | 2.5 | % | |
| Flow : 150°C, 30 min, 0.0230 mm | 2.5 | % | |
| Flow : 150°C, 30 min, 0.0360 mm | 2.5 | % | |
| Flow : 150°C, 30 min, 0.0500 mm | 2.5 | % | |
| Across Flow : 150°C, 30 min, 0.0120 mm | 0.40 | % | |
| Across Flow : 150°C, 30 min, 0.0150 mm | 0.40 | % | |
| Across Flow : 150°C, 30 min, 0.0230 mm | 0.40 | % | |
| Across Flow : 150°C, 30 min, 0.0360 mm | 0.40 | % | |
| Across Flow : 150°C, 30 min, 0.0500 mm | 0.40 | % | |
| Surface Tension | ASTM D2578 | ||
| 15.0 µm | 56 | mN/m | |
| 23.0 µm | 56 | mN/m | |
| 36.0 µm | 56 | mN/m | |
| 50.0 µm | 56 | mN/m | |
| Metallized side : 12.0 µm | 56 | mN/m |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Yield | Internal Method | ||
| 12.0 µm | 59.5 | m²/kg | |
| 15.0 µm | 47.6 | m²/kg | |
| 23.0 µm | 31.0 | m²/kg | |
| 36.0 µm | 19.8 | m²/kg | |
| 50.0 µm | 14.3 | m²/kg |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Optical Density | Internal Method | ||
| 12.0 µm | -2.8 to 7.2 | % | |
| 15.0 µm | -2.8 to 7.2 | % | |
| 23.0 µm | -2.8 to 7.2 | % | |
| 36.0 µm | -2.8 to 7.2 | % | |
| 50.0 µm | -2.8 to 7.2 | % |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 12 15 23 36 50 | µm | |
| Film Thickness - Recommended / Available | 12, 15, 23, 36, 50 µm | ||
| Tensile Strength | ASTM D882 | ||
| MD : Break, 12 µm | 206 | MPa | |
| MD : Break, 15 µm | 186 | MPa | |
| MD : Break, 23 µm | 186 | MPa | |
| MD : Break, 36 µm | 177 | MPa | |
| MD : Break, 50 µm | 167 | MPa | |
| TD : Break, 12 µm | 216 | MPa | |
| TD : Break, 15 µm | 206 | MPa | |
| TD : Break, 23 µm | 206 | MPa | |
| TD : Break, 36 µm | 186 | MPa | |
| TD : Break, 50 µm | 186 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 12 µm | 100 | % | |
| MD : Break, 15 µm | 100 | % | |
| MD : Break, 23 µm | 100 | % | |
| MD : Break, 36 µm | 130 | % | |
| MD : Break, 50 µm | 130 | % | |
| TD : Break, 12 µm | 90 | % | |
| TD : Break, 15 µm | 90 | % | |
| TD : Break, 23 µm | 90 | % | |
| TD : Break, 36 µm | 120 | % | |
| TD : Break, 50 µm | 120 | % | |
| Oxygen Permeability 1 | ASTM D3985 | ||
| 23°C, 12 µm | 0.900 | cm³/m²/24 hr | |
| 23°C, 15 µm | 0.800 | cm³/m²/24 hr | |
| 23°C, 23 µm | 0.800 | cm³/m²/24 hr | |
| 23°C, 36 µm | 0.800 | cm³/m²/24 hr | |
| 23°C, 50 µm | 0.800 | cm³/m²/24 hr | |
| Water Vapor Transmission | ASTM F1249 | ||
| -- 2 | 0.60 | g/m²/24 hr | |
| -- 3 | 0.60 | g/m²/24 hr | |
| -- 4 | 0.60 | g/m²/24 hr | |
| -- 5 | 0.60 | g/m²/24 hr | |
| -- 6 | 0.60 | g/m²/24 hr |
| Note Message | |
|---|---|
| 1 . | 0%RH |
| 2 . | 37.8°C, 90%RH, 36 µm |
| 3 . | 37.8°C, 90%RH, 50 µm |
| 4 . | 37.8°C, 90%RH, 23 µm |
| 5 . | 37.8°C, 90%RH, 12 µm |
| 6 . | 37.8°C, 90%RH, 15 µm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rhelon G1530H-01 | RheTech, Inc. | Nylon 6 | Rhelon |
| Ming Dih EPS S2 | Ming Dih Group Corporation | PS (EPS) | Ming Dih EPS |
| Sindustris PP TE5008B | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| Hanwha Total PP FH51 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| Sylvin 8205-75 White 1482 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |