Makrolon® WB1239
| Category: | PC , Polycarbonate |
| Manufacturer: | Covestro - Polycarbonates |
| Trademark: | Makrolon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gxl4E9_Makrolon-WB1239.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| MVR (300 °C/1.2 kg) 2.0 cm³/10 min; blow molding; high viscosity; branched; food contact quality; extrusion blow molding; injection stretch blow molding; available in transparent colors only; water bottles |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.20 | g/cm³ | ISO 1183 |
| Apparent Density 1 | 0.66 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 2.5 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 2.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage 2 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.80 | % | |
| Flow : 2.00 mm | 0.75 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.30 | % | |
| Equilibrium, 23°C, 50% RH | 0.12 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 108 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2300 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 23°C | 64.0 | MPa | |
| Break, 23°C | 65.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 23°C | 6.6 | % | |
| Break, 23°C | 100 | % | |
| Nominal Tensile Strain at Break (23°C) | > 50 | % | ISO 527-2/50 |
| Flexural Modulus 3(23°C) | 2300 | MPa | ISO 178 |
| Flexural Stress 4 | ISO 178 | ||
| 3.5% Strain, 23°C | 70.0 | MPa | |
| 23°C | 94.0 | MPa | |
| Flexural Strain at Flexural Strength (23°C) 5 | 7.2 | % | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gas Permeation | ISO 2556 | ||
| Carbon Dioxide : 23°C, 100.0 µm | 4200 | cm³/m²/bar/24 hr | |
| Nitrogen : 23°C, 100.0 µm | 140 | cm³/m²/bar/24 hr | |
| Oxygen : 23°C, 100.0 µm | 740 | cm³/m²/bar/24 hr |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flash Ignition Temperature | 480 | °C | ASTM D1929 |
| Self Ignition Temperature | 550 | °C | ASTM D1929 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| ISO Shortname | ISO 7391-PC,B,(,,)-05-9 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Water Vapor Transmission Rate (23°C, 85% RH, 100 µm) | 15 | g/m²/24 hr | ISO 15106-1 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 6 | ISO 7391 | ||
| -30°C, Complete Break | 20 | kJ/m² | |
| 23°C, Partial Break | 75 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -60°C | No Break | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength 7 | ISO 7391 | ||
| -30°C, Partial Break | 55 | kJ/m² | |
| 23°C, Partial Break | 65 | kJ/m² | |
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | ||
| -30°C | 60.0 | J | |
| 23°C | 55.0 | J | |
| Multi-Axial Instrumented Impact Peak Force | ISO 6603-2 | ||
| -30°C | 6400 | N | |
| 23°C | 5500 | N |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 145 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 132 | °C | ISO 75-2/A |
| Glass Transition Temperature 8 | 152 | °C | ISO 11357-2 |
| Vicat Softening Temperature | |||
| -- | 150 | °C | ISO 306/B50 |
| -- | 151 | °C | ISO 306/B120 |
| Ball Pressure Test (144°C) | Pass | IEC 60695-10-2 | |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 55°C | 7.0E-5 | cm/cm/°C | |
| Transverse : 23 to 55°C | 7.0E-5 | cm/cm/°C | |
| Thermal Conductivity 9(23°C) | 0.20 | W/m/K | ISO 8302 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength (23°C, 1.00 mm) | 34 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 23°C, 100 Hz | 3.10 | ||
| 23°C, 1 MHz | 3.00 | ||
| Dissipation Factor | IEC 60250 | ||
| 23°C, 100 Hz | 1.0E-3 | ||
| 23°C, 1 MHz | 0.010 | ||
| Comparative Tracking Index | IEC 60112 | ||
| Solution A | 250 | V | |
| Solution B | 100 | V |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.750 mm | 900 | °C | |
| 1.50 mm | 900 | °C | |
| 3.00 mm | 930 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.750 mm | 900 | °C | |
| 1.50 mm | 900 | °C | |
| 3.00 mm | 900 | °C | |
| Oxygen Index 10 | 26 | % | ISO 4589-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index 11 | 1.587 | ISO 489 | |
| Transmittance | ISO 13468-2 | ||
| 1000 µm | 88.0 | % | |
| 2000 µm | 87.0 | % | |
| 4000 µm | 84.0 | % | |
| Haze (3000 µm) | < 0.80 | % | ISO 14782 |
| Note Message | |
|---|---|
| 1 . | Pellets |
| 2 . | 60x60x2 mm, 500 bar |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 2 mm/min |
| 6 . | Based on ISO 179-1eA, 3 mm |
| 7 . | Based on ISO 180-A, 3 mm |
| 8 . | 10°C/min |
| 9 . | Cross-flow |
| 10 . | Procedure A |
| 11 . | Method A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4582 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Karina BLACK PVC COMPOUND -E 836-48/ 1-Y-CR | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PHOENIX™ 8901 | Phon Tech Industrial Company | TPE | PHOENIX™ |
| Plasmer 5045N/1002 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |
| Sylvin 8200-85UV Clear 8447 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |