FERREX® GPP20CN30AL
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Ferro Corporation |
| Trademark: | FERREX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gwyDlF_FERREX-GPP20CN30AL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FERREX® GPP20CN30AL is a Polypropylene material filled with 21% calcium carbonate. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of FERREX® GPP20CN30AL are:
Typical applications include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 23 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.3 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 65 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 18.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 150 | % | ASTM D638 |
| Flexural Modulus | 1170 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 28.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (23°C) | No Break | ASTM D256 | |
| Gardner Impact | 28.2 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 85.6 | °C | |
| 1.8 MPa, Unannealed | 54.4 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Rear Temperature | 199 to 204 | °C | |
| Middle Temperature | 204 to 210 | °C | |
| Front Temperature | 210 to 216 | °C | |
| Nozzle Temperature | 216 to 221 | °C | |
| Mold Temperature | 46.1 to 60.0 | °C | |
| Back Pressure | 0.138 to 0.345 | MPa | |
| Screw Speed | 100 to 150 | rpm | |
| Clamp Tonnage | 2.8 to 4.1 | kN/cm² | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PONYL 4006G25 | POLYROCKS CHEMICAL CO., LTD | Nylon 6 | PONYL |
| Restramid PA 6 50GF | Polimarky Spolka Jawna | Nylon 6 | Restramid |
| THERMOLAST® M TM4ADT (Series: MC/AD1) | KRAIBURG TPE | TPE | THERMOLAST® M |
| ARC ARC2301 | ARC Resin Corporation | PC | ARC |
| apilon 52bio® DB 40/AP | API SpA | TPU-Polyester | apilon 52bio® |