Styrolution PS 5410
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | INEOS Styrolution Group GmbH |
| Trademark: | Styrolution PS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gwFR2v_Styrolution-PS-5410.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Styrolution PS 5410 is a High Impact Polystyrene product. It can be processed by injection molding and is available in Latin America or North America. Applications of Styrolution PS 5410 include medical/healthcare, packaging and sheet. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Apparent Density 1 | 0.59 to 0.64 | g/cm³ | |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 3.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (L-Scale) | 50 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1690 | MPa | ASTM D638 |
| Tensile Strength (Yield, 23°C) | 17.2 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 50 | % | ASTM D638 |
| Flexural Modulus | 1690 | MPa | ASTM D790 |
| Flexural Strength | 37.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 150 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed) | 82.8 | °C | |
| Vicat Softening Temperature | 98.9 | °C | ASTM D1525 2 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (3.18 mm) | 16 | kV/mm | ASTM D149 |
| Dielectric Constant (1.00 mm, 1 MHz) | 2.50 | ASTM D150 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss (60°) | 15 | ASTM D523 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 182 to 277 | °C | |
| Mold Temperature | 37.8 to 82.2 | °C |
| Note Message | |
|---|---|
| 1 . | without external lubricant |
| 2 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAC® PA-757F | CHI MEI CORPORATION | ABS | POLYLAC® |
| CGPC PVC SO-30X (105 phr Plasticizer E) | China General Plastics Corporation | PVC, Flexible | CGPC PVC |
| Clariant Nylon 6/6 6603-HSL | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Orevac® 9314 | Arkema | EVA | Orevac® |
| EPAMOULD 295A83W | Epaflex Polyurethanes S.R.L. | TPU-Polyester | EPAMOULD |