Generic PC - Carbon Fiber, Nickel-Coated
| Category: | PC , Polycarbonate |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gvtbWG_Generic-PC---Carbon-Fiber-Nickel-Coated.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PC - Carbon Fiber, Nickel-Coated This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.26 - 1.46 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus (23°C) | 6730 - 10500 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 124 - 214 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 53 - 69 | J/m | ASTM D256 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 - 1.0E+4 | ohms | ASTM D257 |
| Volume Resistivity (23°C) | 1.0 - 2.5E+2 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Time | 4.0 | hr | |
| Mold Temperature | 101 - 102 | °C |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PC - Carbon Fiber, Nickel-CoatedThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Miramid® SE15C | BASF Leuna GmbH | Nylon 66 | Miramid® |
| NOVADURAN® 5810G15 | Mitsubishi Engineering-Plastics Corp | PBT Alloy | NOVADURAN® |
| EPT 4021 | Mitsui Chemicals, Inc. | EPDM | EPT |
| Kingfa PBT G30 | Kingfa | PBT | Kingfa PBT |
| LUVOCOM® 1104/XCF/30 VP | Lehmann & Voss & Co. | PEK | LUVOCOM® |