DOW™ HDPE 04852N
| Category: | HDPE , High Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | 陶氏高密度聚乙烯 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gvYfiz_DOWHDPE04852N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOW HDPE 04852N High Density Polyethylene Resin (HDPE) is a narrow molecular weight distribution copolymer designed to offer excellent impact strength and toughness combined with good stiffness. This resin has good processability over a wide range of molding conditions. It is intended for use in injection molding applications such as pails, industrial parts and other shipping containers; it can also be used for structural foamed parts.
Complies with:
Additive:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.952 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.8 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance 1(50°C, 100% Igepal, F50) | 22.0 | hr | ASTM D1693 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 26.9 | MPa | ASTM D638 |
| Fracture | 31.0 | MPa | ASTM D638 |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 10 | % | ASTM D638 |
| Fracture | 1200 | % | ASTM D638 |
| Flexural Modulus 4 | 1100 | MPa | ASTM D790B |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength | 94.6 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature 5 | < -76.1 | °C | ASTM D746 |
| Vicat Softening Temperature | 130 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 131 | °C | Internal method |
| Peak Crystallization Temperature (DSC) | 119 | °C | Internal method |
| Additional Information |
|---|
| Plaque molded and tested in accordance with ASTM D 4976. |
| Note Message | |
|---|---|
| 1 . | Molded and tested in accordance with ASTM D4976 |
| 2 . | Molded and tested in accordance with ASTM D4976. |
| 3 . | Molded and tested in accordance with ASTM D4976. |
| 4 . | Molded and tested in accordance with ASTM D4976. |
| 5 . | Molded and tested in accordance with ASTM D4976. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® C4915 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| SABIC® LLDPE 6821NE | Saudi Basic Industries Corporation (SABIC) | LLDPE | SABIC® LLDPE |
| Shin-Etsu Elastomer KE-2090-40A/B | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| TOTAL Polypropylene PPH 9059 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| Karina YELLOW PVC COMPOUND 602D02/101-C-AT-IS (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |