HIFOR Xtreme® SC74858
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Westlake Chemical Corporation |
| Trademark: | HIFOR Xtreme® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gvP5q2_HIFOR-Xtreme-SC74858.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| WESTLAKE HIFOR Wtreme SC74858 polymer is a high strength, good clarity linear low density polyethylene designed for blown film extrusion that contains no slip or antiblock and processing aid. Films produced with this resin exhibit an excellent toughness. Other features of this resin include good clarity and machine direction tear resistance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.917 | g/cm³ | ASTM D4883 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.50 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD | 186 | MPa | |
| 1% Secant, TD | 207 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Break | 58.6 | MPa | |
| TD : Break | 44.8 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break | 600 | % | |
| TD : Break | 900 | % | |
| Dart Drop Impact | 750 | g | ASTM D1709 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 65 | ASTM D2457 | |
| Haze | 8.0 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALLOY® B1600 | Mitsubishi Chemical Performance Polymers, Inc. | TPE | PRIMALLOY® |
| Ultramid® HPN 9233G HS BK-102 | BASF Corporation | Nylon 6 | Ultramid® |
| Axiall PVC 9113J Clear 13 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| DJSilicone NE-G170 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| Hylac® GP74G5 | Ravago Manufacturing Americas, LLC | ABS | Hylac® |