RTV-2 GI-312B
| Category: | Silicone Rubber, RTV-2 , Silicone Rubber, RTV-2 |
| Manufacturer: | Silicones, Inc. |
| Trademark: | RTV-2 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | guaPyO_RTV-2-GI-312B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
GI-300 series RTV silicone rubbers are two-component, tin-catalyzed systems that cure at room temperature. They are versatile products that are excellent for electrical potting and encapsulation. They can also be used for prototype or production molds to cast polyester, polyurethane or epoxy parts where flexing is not required. They are low viscosity compounds with a variety of hardnesses. The GI-300 series rubbers are not sensitive to inhibition, meaning they will cure at room temperature over virtually any surface. The speed at which the rubbers harden can be accelerated with special activators. The GI-300 series rubbers are especially useful in those applications where outstanding heat resistance and chemical resistance are required. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Specific Gravity | 1.45 | g/cm³ | |
| Shrinkage - Cured | 0.15 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Service Temperature - Cured | -51 to 218 | °C |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coverage - Cured | 0.690 | cm³/g |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| CLTE - Flow | 1.0E-3 | cm/cm/°C | |
| Thermal Conductivity | 0.29 | W/m/K |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 1.0 Mix Ratio by Volume: 15 | ||
| Resin | Mix Ratio by Weight: 10 Mix Ratio by Volume: 100 | ||
| Shelf Life | 26 | wk | |
| Thermoset Mix Viscosity 1 | 15000 to 25000 | cP |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color 2 | Beige | ||
| Viscosity 3 | 30 to 40 | Pa·s | |
| Curing Time | 16 to 18 | hr | |
| Pot Life | 60 to 120 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | |||
| Shore A 4 | 53 to 61 | ||
| Shore A 5 | 56 to 64 | ||
| Tensile Strength | 3.10 | MPa | ASTM D412 |
| Tensile Elongation at Break | 100 | % | ASTM D412 |
| Tear Strength | 4.38 | kN/m | ASTM D624 |
| Arc Resistance | 125 | sec | |
| Electric Strength | 23 | kV/mm | |
| Relative Permittivity (100 Hz) | 3.70 | ||
| Volume Resistivity | 1.0E+13 | ohms·cm | |
| Dissipation Factor (100 Hz) | 0.030 |
| Note Message | |
|---|---|
| 1 . | Mixed |
| 2 . | Base |
| 3 . | Base |
| 4 . | 1 Day |
| 5 . | 7 Days |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Witcom PA66 1L2 | Witcom Engineering Plastics B.V. | Nylon 66 | Witcom PA66 |
| Yuyao PP TL503 | Yuyao Tenglong Plastics Co., Ltd. | PP, Unspecified | Yuyao PP |
| NEXUS PE LLDPE-H118 | Nexus Resin Group, LLC. | LLDPE | NEXUS PE |
| ESENTTIA 08H85DB-P | Polipropileno del Caribe S.A. | PP Homopolymer | ESENTTIA |
| Sylvin 8205-95UV Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |