TECHNYL STAR™ SX 218 V50 BLACK 38N-K
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL STAR™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gtprqv_TECHNYL-STAR-SX-218-V50-BLACK-38N-K.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNYLSTAR™ SX 218 V50 Black 38N-K is based on a patented high flow polyamide 6 resin (Technylstar), heat stabilized, reinforced with 50% of glass fibre, for injection moulding. This product is available in black color. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.55 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 0.33 | -- | % | |
| Flow | 0.25 | -- | % | |
| Water Absorption (23°C, 24 hr) | 0.72 | -- | % | ISO 62 |
| Molding Shrinkage Isotropy | 0.760 | -- | Internal Method |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 17000 | 11600 | MPa | ISO 527-2/1A |
| Tensile Stress (Break) | 230 | 162 | MPa | ISO 527-2/1A |
| Tensile Elongation | ||||
| Break | 2.5 | -- | % | ASTM D638 |
| Break | 2.6 | 4.0 | % | ISO 527-2/1A |
| Flexural Modulus | ||||
| -- | 14000 | -- | MPa | ASTM D790 |
| -- | 15500 | 10000 | MPa | ISO 178 |
| Flexural Strength | 320 | -- | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 15 | 20 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 85 | 95 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ||||
| 23°C | 180 | -- | J/m | ASTM D256 |
| 23°C | 15 | 22 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | 90 | 100 | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 210 | -- | °C | ASTM D648, ISO 75-2/Af |
| Melting Temperature | 222 | -- | °C | ISO 11357-3 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating (3.20 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 230 to 235 | °C | |
| Middle Temperature | 235 to 240 | °C | |
| Front Temperature | 240 to 245 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Safron® C740-25RNA | Safripol (PTY) LTD | PP Impact Copolymer | Safron® |
| TEKAMID™ TA210HI3 | Mando Advanced Materials Co., Ltd. | Nylon 66 | TEKAMID™ |
| APEX® 90-A471R-65-NT | Teknor Apex Company | PVC, Flexible | APEX® |
| LEXAN™ FST3002 resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |
| LubriOne™ NN-30GF/15T Natural UV | PolyOne Corporation | Nylon 66 | LubriOne™ |