Borealis PE FA5224
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Borealis AG |
| Trademark: | Borealis PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gtdei2_Borealis-PE-FA5224.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FA5224 is a Low Density Polyethylene for Film Extrusion. Autoclave Technology. Contains Antioxidant, Anti-block and Medium Slip additives. This grade is developed to give strong film for medium duty applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.2 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic) | 0.15 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| Film Puncture Energy (40 µm) | 2.00 | J | ASTM D5748 |
| secant modulus | ASTM D882A | ||
| MD : 40 µm | 180 | MPa | ASTM D882A |
| TD : 40 µm | 180 | MPa | ASTM D882A |
| Tensile Strength | ISO 527-3 | ||
| MD : 40 µm | 26.0 | MPa | ISO 527-3 |
| TD : 40 µm | 23.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 40 µm | 300 | % | ISO 527-3 |
| TD : Break, 40 µm | 500 | % | ISO 527-3 |
| Dart Drop Impact (40 µm) | 140 | g | ISO 7765-1 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 40 µm | 4.0 | N | ISO 6383-2 |
| TD : 40 µm | 2.0 | N | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 110 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (40.0 µm) | 85 | ASTM D2457 | |
| Haze (40.0 µm) | 8.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 - 190 | °C |
| Extrusion instructions |
|---|
| Draw down: 25 to 30 microns |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RECLAIR® O 21010 | Reliance Industries Limited | LLDPE | RECLAIR® |
| NEFTEKHIM PE 4118Q (18403) | Nizhnekamskneftekhim Inc. | LLDPE | NEFTEKHIM PE |
| AIE PA6 50G3ST | Asia International Enterprise (Hong Kong) Limited | Nylon 6 | AIE PA6 |
| Celstran® +PP-GF40-04CN03/10 | Celanese Corporation | PP, Unspecified | Celstran® |
| Karina BLACK PVC COMPOUND -E 105900-48/ 1-B-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |