Sarlink® TPV X17175B
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPV |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gtEeKC_Sarlink-TPV-X17175B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| The Sarlink 17100 Series are super high flow injection molding grades with excellent UV resistance for exterior applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.921 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore A, 5 sec | 76 | ||
| Shore A, 15 sec | 74 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 37 | ||
| Across Flow : 100% Strain | 2.65 | MPa | |
| Flow : 100% Strain | 3.16 | MPa | |
| Tensile Strength | ISO 37 | ||
| Across Flow : Break | 5.10 | MPa | |
| Flow : Break | 5.20 | MPa | |
| Tensile Elongation | ISO 37 | ||
| Across Flow : Break | 490 | % | |
| Flow : Break | 430 | % | |
| Tear Strength 1 | ISO 34-1 | ||
| Across Flow | 25 | kN/m | |
| Flow | 23 | kN/m | |
| Compression Set | ISO 815 | ||
| 23°C, 22 hr | 26 | % | |
| 70°C, 22 hr | 34 | % | |
| 125°C, 70 hr | 48 | % |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air - Across Flow (150°C, 168 hr) | -20 | % | ISO 37 |
| Change in Tensile Modulus in Air - Across Flow (150°C, 168 hr) | 3.4 | % | ISO 37 |
| Change in Ultimate Elongation in Air - Across Flow (150°C, 168 hr) | -25 | % | ISO 37 |
| Change in Shore Hardness in Air | ISO 868 | ||
| Shore A, 150°C, 168 hr 2 | 1.3 | ||
| Shore A, 150°C, 168 hr 3 | 0.90 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Shear Viscosity - Capillary, 206 1/s (200°C) | 216 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 180 to 205 | °C | |
| Middle Temperature | 180 to 205 | °C | |
| Front Temperature | 180 to 205 | °C | |
| Nozzle Temperature | 185 to 210 | °C | |
| Processing (Melt) Temp | 185 to 210 | °C | |
| Mold Temperature | 10.0 to 55.0 | °C | |
| Back Pressure | 0.100 to 1.00 | MPa | |
| Screw Speed | 100 to 200 | rpm |
| Note Message | |
|---|---|
| 1 . | Method Ba, Angle (Unnicked) |
| 2 . | 15 sec delay |
| 3 . | 5 sec delay |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC P8168 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| SUPREME Specialty PS SP554 | Supreme Petrochem Ltd. | PS (IRPS) | SUPREME Specialty PS |
| Karina IVORY PVC COMPOUND -E 360-IS-SI-SD (FREE) (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| TAFMER™ A-20090S | Mitsui Chemicals, Inc. | PAO | TAFMER™ |
| Sylvin 8627-70 Clear Blue 8301 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |