AKROMID® A3 ICF 40 black (5116)
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gsR4DE_AKROMID-A3-ICF-40-black-5116-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® A3 ICF 40 black (5116) is a 40% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties Applications are mechanically high stressed parts in all industries |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.34 | -- | g/cm³ | ISO 1183 |
| Spiral Flow | 36.0 | -- | cm | Internal Method |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.70 | -- | % | |
| Flow | 0.20 | -- | % | |
| Humidity Absorption - 62% RH (70°C) | 1.5 | -- | % | ISO 1110 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flexural Strain at Break 1 | 1.8 | 2.5 | % | ISO 178 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Reinforcement Content | 40 | -- | % | ISO 1172 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 33000 | 20000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 270 | 200 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.5 | 2.5 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 30000 | 22000 | MPa | ISO 178 |
| Flexural Stress 3 | 370 | 300 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 7.0 | -- | kJ/m² | |
| 23°C | 9.0 | 12 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 55 | -- | kJ/m² | |
| 23°C | 60 | 67 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 255 | -- | °C | ISO 75-2/A |
| Melting Temperature 4 | 262 | -- | °C | DIN EN 11357-1 |
| Thermal Conductivity | 0.47 | -- | W/m/K | DIN 52612 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+3 | 1.0E+3 | ohms | IEC 60093 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 10 K/min, DSC |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYshine PBT D211 | Polykemi AB | PBT | POLYshine |
| Precision Polymer V75W | Precision Polymer Engineering Ltd. | Fluorelastomer | Precision Polymer |
| Sindustris POM FW721F | Sincerity Australia Pty Ltd. | Acetal (POM) Homopolymer | Sindustris POM |
| UBE Nylon 1015GU9 | UBE Industries, Ltd. | Nylon 6 | UBE Nylon |
| NEFTEKHIM PE 4440R (40404) | Nizhnekamskneftekhim Inc. | MDPE | NEFTEKHIM PE |