Hostacom LPX 1702 100015
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gsIDqY_Hostacom-LPX-1702-100015.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hostacom LPX1702 100015 is a copolymer polypropylene 20% Mineral filled. The grade is available in black standard. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/5.0 kg) | 13 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 58.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 23.0 | MPa | |
| Break | 16.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 5.0 | % | |
| Break | 42 | % | |
| Flexural Modulus - Secant | 1900 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C, Complete Break | 3.5 | kJ/m² | |
| 0°C, Complete Break | 5.0 | kJ/m² | |
| 23°C, Complete Break | 10 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 54.0 | °C | ISO 75-2/A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCANAMID 66 A12^F | Polykemi AB | Nylon 66 | SCANAMID 66 |
| Yuyao PP PP Mineral-filled | Yuyao Tenglong Plastics Co., Ltd. | PP, Unspecified | Yuyao PP |
| Grilamid® L 25A NZ | EMS-GRIVORY | Nylon 12 | Grilamid® |
| Keyflex® BT 3047D | LG Chem Ltd. | TPC-ET | Keyflex® BT |
| Sumiliteresin® PR-55438 | SBHPP | Phenolic | Sumiliteresin® |