TECHNYL® 1015CR BRIGHT
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gs9AtS_TECHNYL-1015CR-BRIGHT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6, unfilled, standard for fast injection cycles, for injection moulding |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.14 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 1.5 to 2.0 | -- | % | |
| Flow | 1.3 to 1.7 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.3 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength (Yield) | 90.0 | -- | MPa | ASTM D638 |
| Tensile Elongation (Break) | 30 | -- | % | ASTM D638 |
| Flexural Modulus | 3050 | -- | MPa | ASTM D790 |
| Flexural Strength (Break) | 120 | -- | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | 85 | -- | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | 60.0 | -- | °C | |
| 1.8 MPa, Unannealed | 180 | -- | °C | |
| Melting Temperature | 222 | -- | °C | ISO 11357-3 |
| CLTE - Flow (23 to 85°C) | 7.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+11 | ohms·cm | IEC 60093 |
| Electric Strength | -- | 18 | kV/mm | IEC 60243-1 |
| Dissipation Factor (1 MHz) | 0.020 | 0.10 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 | |
| Glow Wire Flammability Index (0.800 mm) | 675 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 230 to 235 | °C | |
| Middle Temperature | 235 to 245 | °C | |
| Front Temperature | 245 to 250 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RJM SL702 | RJM International, Inc. | PP, Unspecified | RJM |
| ChronoFlex® AR | AdvanSource Biomaterials Corp. | TPU-PC | ChronoFlex® |
| ELASTOSIL® R 401/90 | Wacker Chemie AG | Silicone | ELASTOSIL® R |
| EPLAMID 66 IMP NC C001 | EPSAN Plastik SAN. ve TiC. A.S. | Nylon 66 | EPLAMID 66 |
| Paraclean® 36L45 | INSA | NBR | Paraclean® |